Long term thermal stability of Ni2Al3/Ni hybrid protective coatings formed on creep resistant ferritic steels

Daojie Wu,Jing Wang,Chengyi Zhu,Zhidong Xiang

DOI: https://doi.org/10.3969/j.issn.2095-2783.2013.02.006

2013-01-01

Abstract:Thermal stability was studied at 650℃for hybrid Ni_2Al_3/Ni coatings formed on w_(Cr)= 9%～12%types of creep resistant ferritic steels.The P92 steel was used as a substrate on which two coatings were formed;the thickness of the outer M_2Al_3 layer for both coatings was 22μm,while the thickness of the inner Ni layer was 4μm for one coating and close to 0μm for the other.Both coatings were annealed at 650℃for up to 6 435 h under a protective argon atmosphere.The microstructure and concentration profiles of alloy elements at the cross section were analyzed using SEM/EDS techniques;the phase in the outmost surface was identified by XRD.The results showed that the outer Ni_2Al_3 layer of both coatings was transformed to NiAl at an annealing time of 594 h or less and the newly formed NiAl phase remained stable throughout the rest period of annealing.These findings were consistent with the predictions of thermodynamic analysis.