Abstract:NiCoCrAlTaY coating is widely used in high temperature oxidation resistance, gas erosion protection and gas path sealing of hot-end parts of aeroengines and gas turbines. In this study, NiCoCrAlTaY coatings were prepared on cobalt-based superalloy substrates by high pressure cold spray technology. The microstructure, mechanical property and tribological behaviors of the coatings before and after thermal exposure at 1050 °C were systemically studied. The results showed that NiCoCrAlTaY coatings with very dense structure could be obtained by high-pressure cold spraying with nitrogen as carrier gas. The coating remained completely intimate with the substrate without any cracking and spalling after thermal exposure at 1050 °C for 500 h. Due to elemental diffusion at high temperatures, the coating formed a four-layer structure, including alumina film on the surface, β-NiAl phase depletion layer near the surface, intermediate layer containing β-NiAl phase and β-NiAl phase depletion layer near the substrate. With the prolongation of thermal exposure at 1050 °C, the thicknesses of β-NiAl phase depletion layers both near the surface and the substrate increased. The thickness and content of the intermediate β-NiAl phase layer decreased gradually during thermal exposure. Besides, the average hardness values of the coating rapidly decreased by about 30 % after thermal exposure at 1050 °C for 5 h. In particular, the hardness of the β-NiAl phase depletion layer near the surface substrate was lower than that of the intermediate area containing β-NiAl phase. Due to the microstructure and hardness evolution, the wear resistance of the coating decreased significantly after thermal exposure. The friction coefficient of the coating increased from 0.2 to 0.5, and the volume wear rate of the thermally exposed coating was about 4.5 times higher than that of the as-sprayed coating. The results of this study provide guidance for design and application of high-performance MCrAlY coatings.

Stability of NiCrAlY coating/titanium alloy system under pure thermal exposure

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Effect of vacuum heat treatment on NiCrAlY coating/titanium alloy substrate system

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

High Temperature Behavior of TiAlN Coating Prepared by Arc Ion Plating on TC4 Titanium Alloy

Effect of high temperature exposure on microstructure, mechanical and tribological properties of cold sprayed NiCoCrAlTaY coatings

Microstructure and performance of YTaO4 coating deposited by atmospheric plasma spraying on TC4 titanium alloy surface

Interface stability of NiCrAlY coating without and with a Cr or Mo diffusion barrier on Ti-42Al-5Mn alloy

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

Tribological properties of self-healing NiCrAlY/Cr3C2-Ti3AlC2 coating at high temperatures

Anisotropy of interface characteristics between NiCoCrAlY coating and a hot corrosion resistant Ni-Based single crystal superalloy during thermal exposure at different temperatures

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Isothermal oxidation resistance and microstructure evolution of VPS-TiAlCrY coating on TiAl single crystals at 1100-1200 o C

Effects of High Al Content on the Phase Constituents and Thermal Properties in NiCoCrAlY Alloys

Structural and High-Temperature Oxidation Performance of Al-Co-Y Co-deposited Coatings on a TiAl-Nb Alloy at Low Temperatures

High-temperature oxidation behavior of plasma-sprayed NiCrAlY/TiO2 and NiCrAlY/Cr2O3/YSZ coatings on titanium alloy

Thermal and Thermo-Mechanical Properties of Ti–Al–N and Cr–Al–N Coatings

Oxidation Behaviors of the NiCrAlY Bond Coats in the Thermal Barrier Coatings under External Loads