Abstract:NiCoCrAlTaY coating is widely used in high temperature oxidation resistance, gas erosion protection and gas path sealing of hot-end parts of aeroengines and gas turbines. In this study, NiCoCrAlTaY coatings were prepared on cobalt-based superalloy substrates by high pressure cold spray technology. The microstructure, mechanical property and tribological behaviors of the coatings before and after thermal exposure at 1050 °C were systemically studied. The results showed that NiCoCrAlTaY coatings with very dense structure could be obtained by high-pressure cold spraying with nitrogen as carrier gas. The coating remained completely intimate with the substrate without any cracking and spalling after thermal exposure at 1050 °C for 500 h. Due to elemental diffusion at high temperatures, the coating formed a four-layer structure, including alumina film on the surface, β-NiAl phase depletion layer near the surface, intermediate layer containing β-NiAl phase and β-NiAl phase depletion layer near the substrate. With the prolongation of thermal exposure at 1050 °C, the thicknesses of β-NiAl phase depletion layers both near the surface and the substrate increased. The thickness and content of the intermediate β-NiAl phase layer decreased gradually during thermal exposure. Besides, the average hardness values of the coating rapidly decreased by about 30 % after thermal exposure at 1050 °C for 5 h. In particular, the hardness of the β-NiAl phase depletion layer near the surface substrate was lower than that of the intermediate area containing β-NiAl phase. Due to the microstructure and hardness evolution, the wear resistance of the coating decreased significantly after thermal exposure. The friction coefficient of the coating increased from 0.2 to 0.5, and the volume wear rate of the thermally exposed coating was about 4.5 times higher than that of the as-sprayed coating. The results of this study provide guidance for design and application of high-performance MCrAlY coatings.

Interface stability of NiCrAlY coating without and with a Cr or Mo diffusion barrier on Ti-42Al-5Mn alloy

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

Stability of NiCrAlY coating/titanium alloy system under pure thermal exposure

Microstructure evolution and cyclic oxidation performance of Cr2AlC transition layer as active diffusion barrier for Ni-based superalloy and NiCrAlY coating

Temperature-dependent evolution mechanism of interface microstructure between gradient MCrAlY coatings and nickel-based superalloy

An in-situ formed ceramic/alloy/ceramic sandwich barrier to resist elements interdiffusion between NiCrAlY coating and a Ni-based superalloy

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Study on Microstructure and Oxidation Resistance Mechanism of Y-modified NiCrAlY Coating Prepared by Pack Cementation

Microstructure evolution and interdiffusion behaviors of (Ni,Pt)Al coating with and without Re-diffusion barrier on IC21 substrate at 1100°C

Microstructure and Oxidation Behavior of NiCoCrAlY Coating with Different Sm2O3 Concentration on TiAl Alloy

Improved oxidation resistance of γ-TiAl intermetallics by sputtered Ni+CrAlYHfSiN composite coating

EFFECT OF MCrAlY COATINGS ON OXIDATION RESISTANCE OF TiAl INTERMETALLICS

Oxidation behavior of NiCrAlY coatings with man-made IDZ fabricated by arc ion plating at 1050 °C

Microstructural evolution and element interdiffusion of NiAlHf and NiAlHfY coatings deposited on a Ni-based superalloy

The Interdiffusion Behavior of NiCoCrAlYHf Coating Deposited by Arc Ion Plating on Carburized Ni-Based Single Crystal Superalloy

Oxidation Behavior of Cast Ni3Al Alloys and Microcrystalline Ni3Al+5% Cr Coatings with and without Y Doping

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

Comprehensive study on the microstructure evolution and oxidation resistance performance of NiCoCrAlYTa coating during isothermal oxidation at High temperature

Effect of high temperature exposure on microstructure, mechanical and tribological properties of cold sprayed NiCoCrAlTaY coatings

Improved Oxide Spallation Resistance of Microcrystalline Ni-Cr-Al Coatings