Abstract:The oxidation of bond coat (BC) and interdiffusion between BC layer and superalloys were two mechanisms that contribute to the degradation of thermal barrier coating system (TBCs). The oxidation and interdiffusion of TBCs on single-crystal superalloys were comparatively studied in this work at 950 °C, 1050 °C and 1100 °C over a duration of 1500 h. The results indicated that the thickness of the thermally grown oxide (TGO) progressively increased with the oxidation time and temperature, following a parabolic law. The discontinuous TGO gradually developed into a double-layer structure: the upper layer was a mixed oxide layer, while the lower layer predominantly comprises an Al 2 O 3 layer. Moreover, an interdiffusion zone (IDZ) is formed at the interface between the BC layer and the substrate, with its thickness increasing in response to both temperature and oxidation time. The Cr-rich phases appeared in the IDZ, where Al initially diffused from the BC layer to the substrate, followed by a reverse diffusion process. Simultaneously, Ni and refractory elements diffused from the substrate into IDZ, resulting in the precipitation of the topologically close-packed (TCP) phases and the formation of a secondary reaction zone (SRZ). It has further been shown that Cr-rich phases further diffused into SRZ. Higher oxidation temperatures accelerated the growth of the SRZ and facilitated the transformation of the TCP phases from a blocky to a needle-like morphology. Ultimately, the continuous growth of IDZ and SRZ led to the evolution of the substrate from a monocrystalline to a polycrystalline structure. This study provides valuable data on the microstructural evolution of TBCs and the assessment of their service life.

Microstructure evolution and cyclic oxidation performance of Cr2AlC transition layer as active diffusion barrier for Ni-based superalloy and NiCrAlY coating

Microstructure Evolution and Cyclic Oxidation Performance of Cr2AlC As Active Diffusion Barrier for NiCrAlY Coating on TiAl Alloy

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

A Magnetron Sputtered Microcrystalline Β-Nial Coating for SC Superalloys. Part II. Effects of a NiCrO Diffusion Barrier on Oxidation Behavior at 1100 °C

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

Temperature-dependent evolution mechanism of interface microstructure between gradient MCrAlY coatings and nickel-based superalloy

Improvement of Oxidation-Resistance of NiCrAlY Coatings by Application of CrN or CrON Interlayer

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Microstructure evolution and elemental diffusion behavior near the interface of Cr2AlC and single crystal superalloy DD5 at elevated temperatures

Interface stability of NiCrAlY coating without and with a Cr or Mo diffusion barrier on Ti-42Al-5Mn alloy

High Temperature Oxidation Behaviors of Al/Cr Composite Coating on Ti2AlNb Alloy

Effect of Re-base Diffusion Barrier on the Oxidation Performance of a Gradient NiCoCrAlY Coating

On the Oxidation and Interdiffusion Behavior of an AlCoCrFeNiY High-Entropy Alloy Bond Coat on a Directionally Solidified Ni-based Superalloy

Preparation and cyclic oxidation of gradient NiCrAlYRe coatings on Ni-based superalloys

Microstructure features of cold-sprayed NiCoCrAlTaY coating and its high temperature oxidation behavior

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

Oxidation Behavior of Cast Ni3Al Alloys and Microcrystalline Ni3Al+5% Cr Coatings with and without Y Doping

High temperature oxidation and interdiffusion behavior of recoated NiCoCrAlY coating on a nickel-based superalloy

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

High Temperature Oxidation and Tribological Behavior of Cr3C2-25CoNiCrAlY and Cr3C2-25NiCr Coatings Prepared by AC-HVAF