Abstract:The oxidation of bond coat (BC) and interdiffusion between BC layer and superalloys were two mechanisms that contribute to the degradation of thermal barrier coating system (TBCs). The oxidation and interdiffusion of TBCs on single-crystal superalloys were comparatively studied in this work at 950 °C, 1050 °C and 1100 °C over a duration of 1500 h. The results indicated that the thickness of the thermally grown oxide (TGO) progressively increased with the oxidation time and temperature, following a parabolic law. The discontinuous TGO gradually developed into a double-layer structure: the upper layer was a mixed oxide layer, while the lower layer predominantly comprises an Al 2 O 3 layer. Moreover, an interdiffusion zone (IDZ) is formed at the interface between the BC layer and the substrate, with its thickness increasing in response to both temperature and oxidation time. The Cr-rich phases appeared in the IDZ, where Al initially diffused from the BC layer to the substrate, followed by a reverse diffusion process. Simultaneously, Ni and refractory elements diffused from the substrate into IDZ, resulting in the precipitation of the topologically close-packed (TCP) phases and the formation of a secondary reaction zone (SRZ). It has further been shown that Cr-rich phases further diffused into SRZ. Higher oxidation temperatures accelerated the growth of the SRZ and facilitated the transformation of the TCP phases from a blocky to a needle-like morphology. Ultimately, the continuous growth of IDZ and SRZ led to the evolution of the substrate from a monocrystalline to a polycrystalline structure. This study provides valuable data on the microstructural evolution of TBCs and the assessment of their service life.

The effect of amorphous coating on high temperature oxidation resistance of Ni-based single crystal superalloy

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

Effects of aluminised-coating on microstructure and properties of Ni–Co-base superalloys

Effect of Co distribution on the oxidation behavior of aluminide coatings in Mo-rich Ni-based single-crystal superalloy

Effect of Al2O3 scales from pre-oxidation on the microstructural evolution and phase transition of NiAlHf coatings at 1200 °C

EFFECT OF MCrAlY COATINGS ON OXIDATION RESISTANCE OF TiAl INTERMETALLICS

Effect of Al content on high-temperature oxidation behavior and failure mechanism of CrAl-coated Zircaloy

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Effects of Ni and Cr on the high-temperature oxidation behavior and mechanisms of Co- and CoNi-base superalloys

High-temperature oxidation and hot corrosion of Ni-based single crystal superalloy in the incubation stage

Oxidation behavior of a nickel-based single crystal superalloy at 1100 °C under different oxygen concentration

Effect of Pre-Oxidation on High-Temperature Oxidation Behavior of Al-Si Coating on Nickel-Based Superalloy

AlCoCrNiMo high-entropy alloy as diffusion barrier between NiAlHf coating and Ni-based single crystal superalloy

Microstructure evolution and cyclic oxidation performance of Cr2AlC transition layer as active diffusion barrier for Ni-based superalloy and NiCrAlY coating

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

Improved oxidation resistance of γ-TiAl intermetallics by sputtered Ni+CrAlYHfSiN composite coating

Tuning the secondary reaction zone between PtAl coating and nickel based single crystal superalloy during high-temperature oxidation through regulating aluminizing time

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys