Improvement in oxidation resistance of a Ni3Al-based superalloy IC6 by rhenium-based diffusion barrier coatings

Fengqun Lang,Toshio Narita

DOI: https://doi.org/10.1016/j.intermet.2006.10.042

IF: 4.075

2007-04-01

Intermetallics

Abstract:The oxidation behavior of a Ni3Al-based superalloy IC6 coated with a duplex Re–Cr–Ni–Mo diffusion barrier layer and an Al reservoir layer was investigated in air at 1423K for up to 1080ks. The diffusion barrier layer was formed by electroplating Re(Ni) and Ni films on the alloy, followed by Cr pack cementation at 1573K, and as a result, forms a continuous inner Re–Cr–Ni–Mo diffusion barrier layer and an outer Ni(Cr,Mo,Al) layer. Then a Ni film was electroplated on the Ni(Cr,Mo,Al) layer, followed by Al-pack cementation at 1273K for 18ks, to form an Al reservoir layer with a duplex Ni2Al3 and γ-Ni(Cr,Mo,Al) layers. After oxidation at 1423K in air for 1080ks, the Al reservoir layer changed to a γ-Ni–4Cr–5Mo–12Al (all in at%) layer, on which a protective α-Al2O3 scale formed. The Re–Cr(Mo)–Ni layer was stable and effectively retarded the interdiffusion between the Al reservoir layer and the alloy, as a result, the depth of the microstructural change zone of the alloy was less than 15μm. In contrast, the bare and the coated IC6 superalloy only with an Al reservoir layer were significantly oxidized, accompanied by serious spallation of oxide scales. After oxidation at 1423K for 1080ks, the depth of the microstructural change zone of the alloy was about 200μm for the bare and coated alloy only with an Al reservoir layer. These results indicate that the oxidation resistance of IC6 superalloy can be effectively improved by coating with a Re–Cr–Ni–Mo diffusion barrier layer and an Al reservoir layer.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering