Abstract:The solid dissolution of Fe atoms into Cu matrix induced by mechanical alloying and subsequent thermal decomposition of Fe atoms from the solid solution in composition of Fe60Cu40 have been studied by X-ray diffraction (XRD), Mossbauer spectroscopy and the extended X-ray absorption fine structure (EXAFS) technique. The disappearance of elemental Fe and Cu XRD peaks and the presence of FCC structural XRD peaks illustrate the formation of FCC-Fe60Cu40 solid solution. Meanwhile, the new sextet spectrum with a broadening hyperfine magnetic field distribution also demonstrates that the alloying is on an atomic level and there exist complex coordination environments in the solid solution. EXAFS results Further prove the reality of atomic alloying from the clear observation of Fe atoms taking on FCC coordination in the solid solution. Additionally, a large reduction in the first shell coordination number for a center iron atom but not for a center Cu atom indicates the composition non-uniformity, which suggests that Fe atoms enrich the surface while Cu atoms enrich the core of a FCC nanocrystal. The variation of Mossbauer spectra against the annealing temperatures during thermal decomposition indicates that the Fe atoms at the surface readily nucleate and cluster into alpha -Fe at a temperature slightly below 250 degreesC, whereas the Fe atoms in the core of nano-sized crystals first cluster into gamma -Fe cohering to the FCC matrix at a temperature about 350 degreesC and then transform to alpha -Fe for further annealing at a higher temperature or for a longer time. (C) 2001 Elsevier Science B.V. All rights reserved.

Preparation and granularity control of Fe-Co-Cu prealloyed powder

Effect of Co Addition on the Phase Structure and Magnetic Properties of Fe-Si-Al Alloys

Achieving Homogeneous Fe Distribution and High Strength in Cu-Fe Composite Consolidated by Powder Rolling

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Study of Preparation of Cobalt Aluminate by Sol-Gel Process and Electroless Plating

Hydrothermal Preparation of CuAlO2 Powder

Microstructure and properties of Cu-50Fe alloy produced by chemical co-precipitation and powder metallurgy

Influence of Fabrication Process on Magnetic Properties of Co-Finemet Nanocrystalline Powder Core

Co–Al2O3 nanocomposites powder prepared by electroless plating

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Preparation of Al-5.8%Cu Alloy Semi-Solid Slurry by Controlled Melting

Influence of the material processing on the electrochemical properties of cobalt-free Ml(NiMnAlFe)5 alloy

Nanostructured Composite Obtained by Mechanically Driven Reduction Reaction of Cuo and Al Powder Mixture

Effects of milling process parameters and PCAs on the synthesis of Al0.8Co0.5Cr1.5CuFeNi high entropy alloy powder by mechanical alloying

Preparation of FeAl (B2) intermetallic powder by ball milling and heat treatment

Mechanical Alloying, Fine Structure and Thermal Decomposition of Nanocrystalline Fcc-Fe60cu40

Mechanical alloying of FeAl intermetallic powder for metal injection moulding process

Influences of Master Alloys and Their Preparation Conditions on Microstructures of Semi-solid A356 Alloy Slurries

Thermal Stability and Strengthening Effect of Coherent Precipitates in a (FeCoNi)92Al2.5Ti5.5 High Entropy Alloy