THE EFFECT ON MECHANICAL PROPERTY OF TRANSPARENT ABS RESIN CAUSED BY SBR BI-MODEL PARTICLES

DL Zhang,MY Luan,Q Lin,ZC Cui,B Yang

DOI: https://doi.org/10.3724/sp.j.1105.2006.00356

2006-01-01

Abstract:A series of transparent ABS (T-ABS) resins have been prepared by emulsion in situ suspension polymerization process. It was found that the transparence of T-ABS was satisfactory but the impact strength was lower when smaller SBR particles was used as rubber phase. The transparence of T-ABS was lowered when larger SBR particles were used as rubber phase. When SBR bi-modal particles (S70 nm/S400 nm = 4/6 similar to 6/4, total rubber content 15% to 18%) were used as the dispersion phase, the transparence of ABS resin was higher than 80% and the impact strength was between 90 J/m and 120 J/m. The brittle-tough transition of T-ABS resin using different SBR particles as rubber phase was preliminarily discussed. Synergistic toughening effect of different SBR particles on T-ABS resin was studied. The basic conditions under which the prepared T-ABS resin showed high transparence and satisfactory mechanical properties were found.