Effect of Interface on Brittle - Ductile Transition and Fracture Behavior of ABS/PA6 Blends

SUN Shulin,SUN Lili,ZHANG Huixuan

DOI: https://doi.org/10.13801/j.cnki.fhclxb.2010.04.003

2010-01-01

Abstract:Reactive core-shell modifiers of ABS-g-MA and ABS-g-AA were synthesized to toughen PA6. The difference between the modifiers lays in the reactive monomers on the shell,which would induce different interface properties between the PA6 blends.So the brittle-ductile transition and fracture behavior of the blends were studied when the other parameters were the same.Molau test and torque results indicate ABS-g-MA/PA6 shows superior interface strength.TEM shows ABS-g-MA and ABS-g-AA modifiers disperse in PA6 matrix uniformly.Mechanical test shows brittle-ductile transition takes place between 25%～30%modifiers mass fraction for ABS-g-MA/PA6 blends and impact strength more than 900 J/m is achieved,however,brittle-ductile transition takes place between 30%～35%modifiers mass fraction for ABS-g-AA/PA6 blends.Fracture mechanisms display cavitation of rubber particles and shear yielding of matrix are the major deformation mechanisms for ABS-g-MA/PA6 blends,however,no cavitation can be found and shear yielding is indistinctive for ABS-g-AA /PA6 blends.Vu-Khanh test shows ABS-g-MA/PA6 blends have much higher G_i value and toughness due to the higher interface strength.