Abstract:Based on the analysis of catalyst particle formation and carbon nanotube (CNT) array growth process in floating catalyst chemical vapor deposition (CVD), delicately controlled gaseous carbon sources and catalyst precursors were introduced into the reactor for the controllable growth of CNT array. The low feeding rate of ferrocene was realized through low-temperature sublimation. With less ferrocene introduced into the reactor, the collision among the in situ formed iron atoms decreased, which led to the formation of smaller catalyst particles. The mean diameter of the CNT array, grown at 800(o)C, decreased from 41 to 31 nm when the ferrocene-sublimed temperature reduced from 80 to 60(o)C. Furthermore, low growth temperature was adopted in synthesis, through the modulation of the CNT diameter, by controlling the sintering of catalyst particles and the collision frequency. When the growth temperature was 600(o)C, the as-grown CNTs in the array were with a mean diameter of 10.2 nm. If propylene was used as carbon source, the diameter can be modulated in similar trends. The diameter of CNT can be modulated by the parameter of the operation using the same substrate and catalyst precursor without other equipment or previous treatment. Those results provide the possibility for delicately controllable synthesis of CNT array via simple floating catalyst CVD.

Effect of catalyst particle interspacing on the growth of millimeter-scale carbon nanotube arrays by catalytic chemical vapor deposition

The effects of catalyst treatment on fast growth of millimeter-long multi-walled carbon nanotube arrays

Distortion of carbon nanotube array and its influence on carbon nanotube growth and termination

J2240204 Evaluation of the Properties and Alignment of Carbon Nanotube Sheet Grown by CVD Method

Pretreatment Control of Carbon Nanotube Array Growth for Gas Separation: Alignment and Growth Studied Using Microscopy and Small-Angle X-ray Scattering.

Modulating the Diameter of Carbon Nanotubes in Array Form Via Floating Catalyst Chemical Vapor Deposition

Study of Growth Kinetics of Ultra-Long Carbon Nanotube Arrays Through Wall Number Statistical Investigation

Mass Production of Aligned Carbon Nanotube Arrays by Fluidized Bed Catalytic Chemical Vapor Deposition

Influence of Al2O3 Buffer Layer on Catalyst Morphology and Spinnability of Carbon Nanotube Arrays

Influence of Catalyst Film Thickness Deposited by Atomic Layer Deposition on the Growth of Aligned Carbon Nanotubes

Effects of Temperature and Catalyst Concentration on the Growth of Aligned Carbon Nanotubes

Microstructure Control of Fe Catalyst Films for the Growth of Multiwalled Carbon Nanotube Arrays

How Catalysts Affect the Growth of Single-Walled Carbon Nanotubes on Substrates

Effect of Carbon Deposits on the Reactor Wall During the Growth of Multi-Walled Carbon Nanotube Arrays

Chemical Vapor Deposition of Vertically Aligned Carbon Nanotube Arrays: Critical Effects of Oxide Buffer Layers

Pre-heating effect on the catalytic growth of partially filled carbon nanotubes by chemical vapor deposition

Effect of catalyst on the growth of aligned carbon prepared by microwave chemical vapor deposition

Effects of the Restructuring of Fe Catalyst Films on Chemical Vapor Deposition of Carbon Nanotubes

Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

Regulation on the thickness of aligned carbon nanotube arrays

Influence of Catalyst Thickness on Diameters of Carbon Nanotubes