Abstract:Semiconducting single-walled nanotube (s-SWNT) arrays with specific diameters are urgently demanded in the applications in nanoelectronic devices. Herein, we reported that by using uniform Mo2C solid catalyst, aligned s-SWNT (similar to 90%) arrays with narrow-diameter distribution (similar to 85% between 1.0 and 1.3 nm) on quartz substrate can be obtained. Mo2C nanoparticles with monodisperse sizes were prepared by using molybdenum oxide-based giant clusters, (NH4)(42)[Mo132O372(H3CCOO)(30)(H2O)(72)]. 10H(3)CCOONH(4)center dot 300H(2)O(Mo-132), as the precursor that was carburized by a gas mixture of C2H5OH/H-2 during a temperature-programmed reduction. In this approach, the formation of volatile MoO3 was inhibited due to the annealing and reduction at a low temperature. As a result, uniform Mo2C nanoparticles are formed, and their narrow size-dispersion strictly determines the diameter distribution of SWNTs. During the growth process, Mo2C selectively catalyzes the scission of C-O bonds of ethanol molecules, and the resultant absorbed oxygen (O-ads) preferentially etches metallic SWNTs (m-SWNTs), leading to the high-yield of s-SWNTs. Raman spectroscopic analysis showed that most of the s-SWNTs can be identified as (14, 4), (13, 6), or (10, 9) tubes. Our findings open up the possibility of the chirality-controlled growth of aligned-SWNTs using uniform carbide nanoparticles as solid catalysts for practical nanoelectronics applications.

Atomic Layer Deposition of Al2O3 Catalysts for Narrow Diameter Distributed Single-Walled Carbon Nanotube Arrays Growth

Diameter-Specific Growth Of Semiconducting Swnt Arrays Using Uniform Mo2c Solid Catalyst

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

How Catalysts Affect the Growth of Single-Walled Carbon Nanotubes on Substrates

Multi-Directional Growth of Aligned Carbon Nanotubes Over Catalyst Film Prepared by Atomic Layer Deposition

Selective Growth of Subnanometer Diameter Single-Walled Carbon Nanotube Arrays in Hydrogen-Free CVD.

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Diameter-controlled Growth of Aligned Single-Walled Carbon Nanotubes on Quartz Using Molecular Nanoclusters As Catalyst Precursors

CoPt/CeO2 Catalysts for the Growth of Narrow Diameter Semiconducting Single-Walled Carbon Nanotubes.

Application of NiO deposited by atomic layer deposition for carbon nanotubes catalytic growth

Growth of Single-Walled Carbon Nanotubes with Controlled Structure: Floating Carbide Solid Catalysts

High-Density Growth of Single-Wall Carbon Nanotubes on Silicon by Fabrication of Nanosized Catalyst Thin Films

Growth of Single-Walled Carbon Nanotubes with Different Chirality on Same Solid Cobalt Catalysts at Low Temperature.

Controlling the Diameter of Single-Walled Carbon Nanotubes by Improving the Dispersion of the Uniform Catalyst Nanoparticles on Substrate

Subnanometer Single-Walled Carbon Nanotube Growth from Fe-Containing Layered Double Hydroxides

Diameter‐Selective Density Enhancement of Horizontally Aligned Single‐Walled Carbon Nanotube Arrays by Temperature‐Mediated Method

Towards the preparation of single-walled carbon nanotubes with average diameter of 1.2 nm

Diameter-specific growth of single-walled carbon nanotubes using tungsten supported nickel catalysts

Confined Fe Catalysts for High‐Density SWNT Arrays Growth: a New Territory for Catalyst‐Substrate Interaction Engineering

Growth Of High-Density-Aligned And Semiconducting-Enriched Single-Walled Carbon Nanotubes: Decoupling The Conflict Between Density And Selectivity