Abstract:In the present study, we systematically described the tuning of the diameter of single-walled carbon nanotubes (SWNTs) from individual catalyst particle by temperature-mediated chemical vapor deposition (CVD). The basic idea is to change the temperature quickly during the growth of ultralong SWNTs via a "kite mechanism". It has been found that the diameter of a SWNT varied with temperature oscillation; higher temperature led to thinner SWNTs with the same catalyst particle and lower temperature led to thicker ones. These diameter variations of SWNTs were measured by resonance Raman spectroscopy and atomic force microscopy (AFM). It has also been found that the diameter changes were highly related to their initial diameters. For each initial diameter, there are various probabilities of different diameter changes, but all of them are below a certain maximum, which depends on the initial diameter. The maximum diameter change reaches an extremum of 0.40 nm, while the initial diameter is around 1.6 nm, and the maximum diameter changes are much lower for nanotubes with a larger or smaller diameter, which implies that the diameter mediation by temperature is limited. Based on the results, a well-aligned individual ultralong SWNT array with a narrow diameter distribution of small diameter (around 1.0 nm) or larger diameter (around 2.0 nm) could be grown by ascending or descending temperature-mediated CVD, respectively. At the same time, a simple growth model supposing there is a graphene transition state when the tube formation is initiated is proposed to explain these phenomena. Under this model, the relationship between the growth temperature and the diameter of SWNTs was calculated. It has been found that, a catalyst particle with certain mole fraction of carbon will produce SWNTs with smaller diameter under higher growth temperature and vice versa. This trend accords well with our experimental data. Such diameter modulation of SWNTs by temperature would also help us to understand the CVD growth mechanism of SWNTs.

Diameter‐Selective Density Enhancement of Horizontally Aligned Single‐Walled Carbon Nanotube Arrays by Temperature‐Mediated Method

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Growth Of High-Density-Aligned And Semiconducting-Enriched Single-Walled Carbon Nanotubes: Decoupling The Conflict Between Density And Selectivity

Microwave Purification of Large-Area Horizontally Aligned Arrays of Single-Walled Carbon Nanotubes

Spatially Confined CVD Growth of High‐Density Semiconducting Single‐Walled Carbon Nanotube Horizontal Arrays

Selective Growth of Subnanometer Diameter Single-Walled Carbon Nanotube Arrays in Hydrogen-Free CVD.

Growth of High-Density Horizontal SWNT Arrays Using Multi-Cycle In-Situ Loading Catalysts

Diameter-Specific Growth Of Semiconducting Swnt Arrays Using Uniform Mo2c Solid Catalyst

Large-area Growth of Ultra-High-density Single-Walled Carbon Nanotube Arrays on Sapphire Surface

Growth of High-Density Horizontal SWNT Arrays by Pre-Cracking of Carbon Source

Increasing the Density of Single-Walled Carbon Nanotube Arrays by Multiple Catalysts Reactivation

Confined Fe Catalysts for High‐Density SWNT Arrays Growth: a New Territory for Catalyst‐Substrate Interaction Engineering

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Using Nanoscale Thermocapillary Flows to Create Arrays of Purely Semiconducting Single-Walled Carbon Nanotubes

Tuning the Diameter of Single-Walled Carbon Nanotubes by Temperature-Mediated Chemical Vapor Deposition

Growth of Horizontal Semiconducting SWNT Arrays with Density Higher Than 100 Tubes/μm Using Ethanol/Methane Chemical Vapor Deposition

Fabrication of Dense Horizontally Aligned Arrays of Single-Wall Carbon Nanotubes from Vertically Aligned Arrays

Importance of diameter control on selective synthesis of semiconducting single-walled carbon nanotubes.

Growth of Homogeneous High‐Density Horizontal SWNT Arrays on Sapphire Through a Magnesium‐Assisted Catalyst Anchoring Strategy

Electric-field-enhanced assembly of single-walled carbon nanotubes on a solid surface.

Growth of high-density horizontally aligned SWNT arrays using Trojan catalysts