Abstract:A simple, room-temperature bonding process was developed for the fabrication of glass microfluidic chips. High-quality bonding with high yields (>95%) was achieved without the requirement of clean room facilities, programmed high-temperature furnaces, pressurized water sources, adhesives, or pressurizing weights. The plates to be bonded were sequentially prewashed with acetone, detergent, high-flow-rate (10-20 m/s) tap water, and absolute ethyl alcohol and were soaked in concentrated sulfuric acid for 8-12 h. The plates were again washed in high-flow-rate tap water for 5 min and, finally, with demineralized water. The plates were bonded by bringing the cleaned surfaces into close contact under a continuous flow of demineralized water and air-dried at room temperature for more than 3 h. This bonding process features simple operation, good smoothness of the plate surface, and high bonding yield. The procedures can be readily applied in any routine laboratory. The bonding strength of glass chips thus produced, measured using a shear force testing procedure, was higher than 6 kg/cm(2). The mechanism for the strong bonding strength is presumably related to the formation of a hydrolyzed layer on the plate surfaces after soaking the substrates in acid or water for extended periods. Microfluidic chips bonded by the above procedure were tested in the CE separation of fluorescein isothiocyanate-labeled amino acids.

A Rapid and Low-Cost Procedure for Fabrication of Glass Microfluidic Devices

Micro Fabrication of Micro Fluidic Glass Chip Without Clean Room Condition

A Simplified Microfabrication Technology For Production Of Glass Microfluidic Chips

Rapid Prototyping of Soft Lithography Masters for Microfluidic Devices Using Dry Film Photoresist in a Non-Cleanroom Setting

Bonding of Glass-Based Microfluidic Chips at Low- or Room-Temperature in Routine Laboratory

Fabrication of full glass chips with hybrid micro- and nanochannels and their application to protein concentration

Fabricating Microstructures on Glass for Microfluidic Chips by Glass Molding Process

Micro Etching Method Inside Microchannels

Fabrication Of Microfluidic Chips By An Ultrasonic Micromachining With Wet-Etch Smoothing Method On Glass Substrates

Fabrication of Micro/Nanofluidic Chip on Glass Substrate and Its Application for Electrokinetic Concentration of Proteins

Microchannel Fabrication on Glass Materials for Microfluidic Devices

Glass etching to bridge micro- and nanofluidics.

Fabrication Of Microfluidic Devices In Silica Glass By Water-Assisted Ablation With Femtosecond Laser Pulses

A simple approach to fabricate multi-layer glass microfluidic chips based on laser processing and thermocompression bonding

Fabrication of Fluidic Chips with 1-D Nanochannels on PMMA Substrates by Photoresist-Free UV-lithography and UV-assisted Low-Temperature Bonding

Fabrication of 1-d nanochannels on PMMA substrate by photoresist-free uv lithography and UV-assisted bonding under low temperature

A Novel Restricted-Flow Etching Method for Glass

Preparation of hybrid soda-lime/quartz glass chips with wettability-patterned channels for manipulation of flow profiles in droplet-based analytical systems.

Route to one-step microstructure mold fabrication for PDMS microfluidic chip

Bonding of Glass Microfluidic Chips at Room Temperatures

Paper-based microfluidics with high resolution, cut on a glass fiber membrane for bioassays.