Abstract:Mullite nanocomposites powders were successfully synthesized from high-aluminium coal fly ash,coal gangue,andalusite-sericite phyllite and oil shale slag through the hydrothermal crystallization process after the removal of the residual carbon,deferrization or calcination.The phase constitution and microstructure of the synthesized mullite nanocomposites powders were investigated by X-ray diffraction(XRD),transmission electron microscopy(TEM),selected area electron diffraction(SAED) and energy-dispersive X-ray(EDX).Moreover,the reaction mechanism was analyzed according to MAS-NMR results.The experimental results show that mullite nanocomposites powders can be prepared from any silicon-aluminium-bearing minerals at 80~90℃ for 3 h with NaOH concentration of 2~4 mol/L and L/S ratio(liquid/solid ratio in mass) of 10 mL/g.Mullite nanocomposites which are synthesized from coal gangue,andalusite-sericite phyllite and oil shale slag are mainly existent as whole puncheon-shaped crystals,whose average lengths are 50 nm,300 nm and 150 nm,and whose average aspect ratios are 4,3.5 and 3.75,respectively.Otherwise,when coal fly ash is used as the raw material,mullite nanocomposites are mainly rod-like,acicular and fibroid in shape with the length in the range of 30~80 nm and the diameter in the range of 4.5~30 nm.MAS-NMR analysis indicates that the nano-size mullite grows around the central atoms Al,Si of the O4 tetrahedron and the growth unit Al-4 is existent in this process definitely.

A new chemical method for preparation of both pure and doped mullite

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Chemical Synthesis and Conductivity Study of Doped Mullite Solid-Solutions

Mullite Fibers Prepared by Sol-Gel Method Using Aluminum Chloride Aluminum Isopropoxide and Tetraethylorthosilicate

Mullite Fibers Prepared from an Inorganic Sol–gel Precursor

Preparation of Mullite Fibres by Sol–gel Processes Using Aluminium Carboxylates and Tetraethylorthosilicate

Preparation of Mullite Fibers by Sol-Gel Process and Study of Their Morphology

Fabrication of ultrafine mullite powders

Synthesis and Controlled Growth of Mullite Submicron Powders

The Preparation of Mullite Nanocomposites Powders from Silicon-Aluminium- Bearing Minerals Through Hydrothermal Crystallization

Fabrication of Fine Mullite Powders by Heterogeneous Nucleation and Growth Processing

Fabrication of Mullite Powders by A Novel Processing

Preparation of Mullite from Low-grade Kaolin

Synthesis and Characterization of Ti, Fe-Doped Mullite-I

Molten Salt Synthesis of Mullite Whiskers from Silicon Carbide Precursor

Preparation of Nanometer Mullite Via Supercritical CO2

Preparation of Nanometer Mullite via Supercritical CO<sub>2</sub>

Mullite Fibres Preparation by Aqueous Sol–gel Process and Activation Energy of Mullitization

Preparation of Mullite Monoliths with Well-Defined Macropores and Mesostructured Skeletons Via the Sol–gel Process Accompanied by Phase Separation

High purity mullite ceramics by reaction sintering

Preparation and Mechanism of Nano Mullite Powders from Kaolin Via Open Hydrothermal Process.