Densification, Microstructure Evolution, and Mechanical Properties of Low-Temperature-Sintered 90W-4.9Ni-2.1fe-3cu Alloy
Zhu Wentan,Liu Wensheng,Ma Yunzhu,Cai Qingshan,Wang Jianning,Duan Youteng
DOI: https://doi.org/10.1007/s11665-021-05539-0
IF: 2.3
2021-01-01
Journal of Materials Engineering and Performance
Abstract:In this work, a 90W-4.9Ni-2.1Fe-3Cu alloy was developed for low-temperature sintering. Conventional 90W-7Ni-3Fe alloy, which is typically manufactured at 1500 °C, was synthesized at the same sintering conditions for comparison. In the low-temperature range from 1250 to 1400 °C, sintering densification, microstructure evolution, and mechanical properties were systematically investigated. For the 90W-4.9Ni-2.1Fe-3Cu alloy, a rapid specimen densification occurs at 1350 °C due to liquid formation over the temperature range from 1328 to 1370 °C. The maximum relative density of 99.01% of the alloy is reached at 1400 °C. According to electron probe microanalysis (EPMA) and transmission electron microscopy (TEM), the alloy is composed of a W phase and a γ-(Ni, Fe, Cu) matrix phase, which is well bonded with W grains. The orientation relationship of these two phases can be described as [001] γ-(Ni, Fe, Cu)∥[ $$\bar{1}$$ 33]W. The tensile strength and hardness of the sintered alloy increase with increasing sintering temperature. At 1400 °C, the tensile strength of the 90W-4.9Ni-2.1Fe-3Cu alloy is with 874 MPa considerably higher than that of the 90W-7Ni-3Fe alloy (385 MPa). The formation mechanism of γ-(Ni, Fe, Cu) phase is included in the discussion.