Abstract:In this paper, the bending fatigue behavior of a high density (7.30 similar to 7.40g/cm(3)) Fe-2Cu-2Ni-1Mo-1C material, which was fabricated by die-wall lubricated warm compaction of partially-diffuse alloyed powder, was studied by ultrasonic fatigue testing. Influence of heat-treatment on the bending fatigue behavior of the sintered material was discussed. Results showed that the S-N curve of the sinter-hardened material decreased continually without the presence of the traditional horizontal plateau. Fatigue strength was 194, 239, 293 and 360 MPa at 10(8), 10(7), 10(6) and 10(5) cycles, respectively. After heat treatment, the S-N curve displayed the characteristic of "multi-stage type", and two decreasing curves, which was separated by a horizontal plateau in the region of 10(5)similar to 10(7) cycles. The fatigue failure yet occured in the regime of exceeding 10(7) cycles. Fatigue strength was 205, 293, 419 and 549 MPa at 10(8), 10(7), 10(6) and 10(5) cycles, respectively, after heat treatment. Fatigue strength after heat-treatment was higher than those in sinter-hardened state indicated that appropriate heat-treatment could improve the fatigue strength of P/M materials. Scanning electron microscopy revealed that cracks initiated from large pores or defects on the surface or near the sub-surface. Cracks propagated through trans-crystalline and inter-granular modes. Cleavage fracture and typical fatigue striations were observed in the crack propagation region of the sintered sample. Evidence of dimple ductile fracture was found in the rupture region of the samples.

STUDY ON THE SINTER-HARDENING PROPERTIES OF Fe-Cu-Ni-Mo-C MATERIALS BY WARM COMPACTION WITH WALL LUBRICATED DIE

Sinter-hardening properties of partially-diffuse alloyed Fe-Cu-Ni-Mo-C material prepared by die wall lubricated warm compaction

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Study on the Mechanical Properties and Microstructure of Partially-diffuse Alloyed Fe-Cu-Ni-Mo-C Materials

Effects of Cooling Rate and Carbon Content on Microstructure and Mechanical Properties of Fe-Cu-Ni-Mo-C Sintered Materials

Influence of Sintering Parameters on Tensile Strength of Warm Compacted Fe-2Ni-2Cu-1Mo-1C Material

Study on sintering behaviors of warm compacted Fe-2Ni-2Cu-lMo-lC material in die wall lubrication

Study on High Performance Warm Compacted Fe-2Ni-2Cu-1Mo-1C Powder Metallurgy Materials

Study on Bending Ultrasonic Fatigue Behavior of Sinter-Hardened Fe-2Cu-2Ni-1Mo-1C Materials Prepared by Warm Compaction

Study on fatigue behavior of Fe-2Cu-2Ni-1Mo-1C powder metallurgy material

Properties and sintering behaviors of Fe-Cu-Mn-C alloy

Die wall lubricated warm compacting and sintering behaviors of pre-mixed Fe–Ni–Cu–Mo–C powders

High Strength Sinter-Hardening Powder Metallurgy Alloys

Die Wall Lubricated Warm Compaction of Fe-Ni-Cu-Mo-C Powders

Sintering Behavior and Properties of Mo-Cu Composites

Improved Homogenization of Ni in Sintered Steels Through the Use of Cr-Containing Prealloyed Powders

Effect of Sintering Parameters on Warm Compacted Iron-Based Material

Warm Compacting Behavior of W-Ni-Fe Alloy with Different Lubricant Contents

Effects of Alloy Composition on Microstructure and Mechanical Properties of Iron-Based Materials Fabricated by Ball Milling and Spark Plasma Sintering

Influence of Ni-P content on microstructure and mechanical properties of Fe-x(Ni+P)-1Cu alloys

ULTRASONIC FATIGUE BEHAVIOR OF A Fe-BASED WARM-COMPACTED POWDER METALLURGY MATERIAL