Abstract:In this paper, the bending fatigue behavior of a high density (7.30 similar to 7.40g/cm(3)) Fe-2Cu-2Ni-1Mo-1C material, which was fabricated by die-wall lubricated warm compaction of partially-diffuse alloyed powder, was studied by ultrasonic fatigue testing. Influence of heat-treatment on the bending fatigue behavior of the sintered material was discussed. Results showed that the S-N curve of the sinter-hardened material decreased continually without the presence of the traditional horizontal plateau. Fatigue strength was 194, 239, 293 and 360 MPa at 10(8), 10(7), 10(6) and 10(5) cycles, respectively. After heat treatment, the S-N curve displayed the characteristic of "multi-stage type", and two decreasing curves, which was separated by a horizontal plateau in the region of 10(5)similar to 10(7) cycles. The fatigue failure yet occured in the regime of exceeding 10(7) cycles. Fatigue strength was 205, 293, 419 and 549 MPa at 10(8), 10(7), 10(6) and 10(5) cycles, respectively, after heat treatment. Fatigue strength after heat-treatment was higher than those in sinter-hardened state indicated that appropriate heat-treatment could improve the fatigue strength of P/M materials. Scanning electron microscopy revealed that cracks initiated from large pores or defects on the surface or near the sub-surface. Cracks propagated through trans-crystalline and inter-granular modes. Cleavage fracture and typical fatigue striations were observed in the crack propagation region of the sintered sample. Evidence of dimple ductile fracture was found in the rupture region of the samples.

Study on the Mechanical Properties and Microstructure of Partially-diffuse Alloyed Fe-Cu-Ni-Mo-C Materials

STUDY ON THE SINTER-HARDENING PROPERTIES OF Fe-Cu-Ni-Mo-C MATERIALS BY WARM COMPACTION WITH WALL LUBRICATED DIE

Sinter-hardening properties of partially-diffuse alloyed Fe-Cu-Ni-Mo-C material prepared by die wall lubricated warm compaction

Study on High Performance Warm Compacted Fe-2Ni-2Cu-1Mo-1C Powder Metallurgy Materials

Effects of Cooling Rate and Carbon Content on Microstructure and Mechanical Properties of Fe-Cu-Ni-Mo-C Sintered Materials

Properties and sintering behaviors of Fe-Cu-Mn-C alloy

Study on sintering behaviors of warm compacted Fe-2Ni-2Cu-lMo-lC material in die wall lubrication

Influence of Sintering Parameters on Tensile Strength of Warm Compacted Fe-2Ni-2Cu-1Mo-1C Material

Die wall lubricated warm compacting and sintering behaviors of pre-mixed Fe–Ni–Cu–Mo–C powders

Study on fatigue behavior of Fe-2Cu-2Ni-1Mo-1C powder metallurgy material

Improvement In Microstructure Homogeneity Of Sintered Compacts Through Powder Treatments And Alloy Designs

Investigation on sintering and deformation strengthening of Mo-Cu alloy

Sintering Behavior and Properties of Mo-Cu Composites

The sintering behavior of ultra-fine Mo-Cu composite powders and the sintering properties of the composite compacts

Improvements in Microstructure Homogenization and Mechanical Properties of Diffusion-Alloyed Steel Compact by the Addition of Cr-Containing Powders

Surface morphology and technical performances of warm compaction powder made by various methods

Effect of small amount of Mo addition on microstructure and mechanical properties of Fe-0.5Mn-0.5C sintered steels

Study on Mechanical Properties and Microstructure of Cu20Fe80 Alloy Using the Mechanical Alloying

High Density Sintering of the Diffusible Alloyed Powder

Improved Homogenization of Ni in Sintered Steels Through the Use of Cr-Containing Prealloyed Powders

Study on Bending Ultrasonic Fatigue Behavior of Sinter-Hardened Fe-2Cu-2Ni-1Mo-1C Materials Prepared by Warm Compaction