Microstructure evolution, phase decomposition and transition of Al0.8Co0.5Cr1.5CuFeNi HEA during high temperature sintering and mechanical properties corresponding to different microstructures

Minjie Huang,Jufu Jiang,Ying Wang,Yingze Liu,Ying Zhang

DOI: https://doi.org/10.1016/j.matdes.2022.111167

IF: 9.417

2022-01-01

Materials & Design

Abstract:Microstructure evolution, phase determination, phase decomposition and transition of mechanically alloyed Al0.8Co0.5Cr1.5CuFeNi during 950-1150 t high temperature sintering, and the effect of sintered microstructures on mechanical properties were investigated. The microstructure was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM). Cu separation occurred first, needle-like Cu rich precipitation in the BCC matrix formed the nucle-ation sites of Al-Ni rich decomposition, while fine lath separation and Cu rich decomposition region sur-rounding the FCC matrix were formed in the FCC matrix, and the remaining FCC matrix formed L12 order. Ordered Al-Ni rich decomposition in BCC matrix appeared after 1000 t sintering. As sintering tempera-ture increased, Al-Ni rich decomposition increased and coarsened and length-width ratio increased. a phase precipitated after 950 t, 1000 t and 1050 t sintering, and disappeared as sintering temperature was higher than 1100 t. Yield strength of sintered alloy decreased from 1445.9 MPa to 1151.5 MPa, and hardness decreased from 714.2 HV to 536.3 HV as sintering temperature increased. The significant increase in plasticity after 1100 t and 1150 t was due to dissolution of a phase. Dislocation accumula-tion around a phase caused development of micro cracks and reduced the plasticity.(c) 2022 Published by Elsevier Ltd. This is an open access article under the CC BY-NC-ND license (http:// creativecommons.org/licenses/by-nc-nd/4.0/).