The Effect of Heat Treatment on the Microstructure and Mechanical Properties of Al0.6CoFeNi2V0.5 High Entropy Alloy

Hui Liang,Jinxin Hou,Li Jiang,Zhaoxin Qi,Min Zhang,Zhiqiang Cao
DOI: https://doi.org/10.3390/coatings14060658
IF: 3.236
2024-05-23
Coatings
Abstract:Al0.6CoFeNi2V0.5 high entropy alloy was successfully designed and prepared via the nonconsumable arc-melting process, and it was annealed at 600 °C, 800 °C, and 1000 °C for 4 h. Its microstructure and mechanical properties were studied. The as-cast alloy consisted of FCC and BCC phases, and no phase transformation occurred during annealing at 600 °C. Hard Al3V-type metal compounds precipitated during annealing at 800 °C, and BCC particles precipitated in the FCC matrix during annealing at 1000 °C. After annealing, the strength and hardness of Al0.6CoFeNi2V0.5 high-entropy alloy both showed a decreasing trend, because the annealing process eliminated the internal stress in this alloy. However, as the annealing temperature increased, the strength and hardness of the Al0.6CoFeNi2V0.5 high-entropy alloy samples gradually increased. This is because the hard Al3V metal compounds precipitated when the annealing temperature was 800 °C, which produced the "second phase strengthening" effect. At 1000 °C, the larger volume fraction of the hard and fine BCC phase (21.81%) diffusely precipitated; the precipitation of this BCC phase not only produced a "second phase strengthening" effect, which also resulted in "solid solution strengthening", ultimately exhibiting enhanced hardness and strength. These findings have important theoretical reference value for the study of the microstructure and mechanical properties of high-entropy alloys. And, this study plays a significant role in promoting the research and development of new component materials that bear compressive loads, such as columns in large factory buildings, supports for cranes, and clamping bolts for rolling mills in practical mechanical engineering.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
This paper aims to study the influence of heat treatment on the microstructure and mechanical properties of Al<sub>0.6</sub>CoFeNi<sub>2</sub>V<sub>0.5</sub> high - entropy alloy. Specifically, the authors prepared this high - entropy alloy by non - consumable arc melting method and carried out annealing treatment at 600°C, 800°C and 1000°C for 4 hours to observe how the annealing treatment at different temperatures affects the microstructure and mechanical properties of the alloy. ### Research Background High - entropy alloys (HEAs) are a new type of alloy material, breaking through the traditional alloy design concept. High - entropy alloys are usually composed of 5 to 13 elements, and the content of each main element is between 5 at.% and 35 at.%. This alloy design expands the possibility of alloy design from the edge and corner areas of the phase diagram to the intermediate area. Due to their high mixing entropy, high - entropy alloys tend to form simple solid - solution structures and exhibit unique high - entropy effects, sluggish diffusion effects, lattice distortion effects and cocktail effects, and have characteristics such as high strength, high hardness, good wear - resistant and corrosion - resistant properties, excellent high - temperature stability and macroscopic superconductivity. ### Research Purpose The main purpose of this study is to explore the influence of different annealing temperatures (600°C, 800°C and 1000°C) on the microstructure and mechanical properties of Al<sub>0.6</sub>CoFeNi<sub>2</sub>V<sub>0.5</sub> high - entropy alloy. Specific objectives include: 1. **Microstructure Analysis**: Study the phase composition and microstructure of the alloy at different annealing temperatures by means of X - ray diffraction (XRD) and electron probe micro - analysis (EPMA). 2. **Mechanical Property Testing**: Evaluate the strength and hardness of the alloy at different annealing temperatures through compression tests and Vickers hardness tests. ### Main Findings 1. **Microstructure**: - The as - cast alloy is composed of FCC and BCC two phases. - After annealing at 600°C, the alloy still maintains the FCC + BCC structure without obvious changes. - After annealing at 800°C, hard Al<sub>3</sub>V - type metal compounds are precipitated in the BCC matrix, producing a second - phase strengthening effect. - After annealing at 1000°C, a fine BCC phase with a large volume fraction (21.81%) is precipitated in the FCC matrix, which not only produces a second - phase strengthening effect but also leads to solid - solution strengthening, and finally shows enhanced hardness and strength. 2. **Mechanical Properties**: - The yield strength of the as - cast alloy is 426.6 MPa, and the hardness is 263.7 HV. - After annealing at 600°C, the yield strength drops to 353.4 MPa, and the hardness drops to 216.9 HV. - After annealing at 800°C, the yield strength rises to 383.8 MPa, and the hardness rises to 251.8 HV. - After annealing at 1000°C, the yield strength further rises to 401.1 MPa, and the hardness rises to 261.3 HV. ### Conclusion This study reveals the influence of different annealing temperatures on the microstructure and mechanical properties of Al<sub>0.6</sub>CoFeNi<sub>2</sub>V<sub>0.5</sub> high - entropy alloy. With the increase of annealing temperature, the hardness and strength of the alloy gradually increase, which is mainly due to the combined effect of second - phase strengthening and solid - solution strengthening. These findings have important theoretical reference value for the research on the microstructure and mechanical properties of high - entropy alloys, and are of great significance for the development of new pressure - bearing materials (such as columns in large - scale factories, supports of cranes and clamping bolts of rolling mills).