Effect of Cold Deformation and Heat Treatment on the Microstructure and Mechanical Behavior of High Entropy Alloy CuCrFeNi2Al0.5

Jinhong Pi,Changfu Yu,Chao Sun,Hailong Du,Yinlong Fan,BaoSen Zhang,Shaofeng Yang
DOI: https://doi.org/10.1007/s11665-018-3822-8
IF: 2.3
2018-12-18
Journal of Materials Engineering and Performance
Abstract:CuCrFeNi2Al0.5, a high entropy alloy (HEA) with a single FCC phase, was deformed at room temperature and then heat treated. The small particles precipitated from the deformed FCC solid solution matrix after heating at 700 °C, softening the solid solution matrix. This outcome confirms that the microstructure of HEAs can be controlled by heat treatment in addition to controlling the chemical composition and the rate of cooling from liquid alloys. The hardness of the samples increased due to precipitation hardening, and the specimen heated at 700 °C with 10% predeformation had the highest hardness. As the predeformation increases, the precipitates tend to interweave in the network morphology. Meanwhile, grains in all specimens became more severely coarse after heat treatment at 1100 °C. Predeformation followed by annealing can obviously slow down the creep rate, indicating that annealing at an appropriate temperature can improve the mechanical properties of deformed HEA.
materials science, multidisciplinary
What problem does this paper attempt to address?