High temperature deformation behavior of dual-phase Al0.6CoCrFeNi high-entropy alloys

Tangqing Cao,Lili Ma,Lu Wang,Jinlian Zhou,Yangwei Wang,Benpeng Wang,Yunfei Xue

DOI: https://doi.org/10.1016/j.jallcom.2020.155305

IF: 6.2

2020-09-01

Journal of Alloys and Compounds

Abstract:<p>The deformation behavior of dual-phase (FCC + BCC) Al_0.6CoCrFeNi high-entropy alloy (HEA) was investigated in a temperature range from 900 °C to 1200 °C and a strain rate range from 10⁻³ to 1 s⁻¹. The BCC phase completely recrystallized when the deformation temperature exceeded 1100 °C, while the FCC phase did not even at 1200 °C. Continuing annealing at high temperature with long time (1200 °C for 20 h) can achieve an optimized microstructure, exhibiting that the island-shaped BCC phase uniformly distributed in the FCC phase with a fine equiaxed grain. Compared with the as-cast alloys, the annealed alloy shows an obvious increase in fracture strain with a relatively low decrease in yield stress, demonstrating that such a thermo-mechanical process is feasible for improving the mechanical property of dual-phase HEAs.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper aims to study the deformation behavior of dual - phase (face - centered cubic + FCC + body - centered cubic + BCC) Al_0.6CoCrFeNi high - entropy alloy at high temperatures. Specifically, the author experimentally explored the high - temperature deformation characteristics of this alloy in the temperature range from 900 °C to 1200 °C and the strain rate range from 10^-3 to 1 s^-1. The focus of the study is to understand the microstructural evolution of the FCC and BCC phases in the alloy and their influence on mechanical properties under different temperature and strain rate conditions.

The main findings of the paper include:
1. **Microstructural evolution**: When the deformation temperature exceeds 1100 °C, the BCC phase is fully recrystallized, while the FCC phase does not recrystallize even at 1200 °C. Long - term high - temperature annealing (such as annealing at 1200 °C for 20 hours) can achieve an optimized microstructure, in which the island - like BCC phase is uniformly distributed in the FCC phase of fine equiaxed grains.
2. **Improvement of mechanical properties**: Compared with the as - cast alloy, the heat - treated alloy shows a significant increase in fracture strain (an increase of 68.4%) and a relatively small decrease in yield stress (a decrease of 23.9%). This indicates that thermomechanical processing can effectively improve the mechanical properties of dual - phase high - entropy alloys.

Through these studies, the author hopes to provide a deeper understanding of the deformation mechanism of dual - phase high - entropy alloys under high - temperature conditions and promote the industrial application of such materials.