Abstract:The microstructure of peritectic alloys of important applications determines the final properties of them. The growth of peritectic β phase which greatly influences the structure of peritectic systems is divided into three different types: peritectic reaction at TP: L + α → β, then solid-state peritectic transformation α → β and direct precipitation L → β. In addition to transparent organic systems, peritectic transformation was always analyzed using interrupted directional solidification during which the sample is kept stationary after experiencing a distance of directional growth. Then, the growth of β phase through peritectic transformation is accompanied with the migration of the α/β interface towards α phase below TP. However, it is found in SnNi peritectic system (L + Ni3Sn2 → Ni3Sn4) that the migration rate of Ni3Sn2/Ni3Sn4 interface is much larger than that of peritectic transformation. Further examination shows that this interface migration can also be induced by the diffusion-controlled liquid migration initiating at the Ni3Sn2/Ni3Sn4 interface. Based on the model describing the liquid migration process, the migration of the Ni3Sn2/Ni3Sn4 interface through liquid migration is predicted, which matches well with the experimental measurement. This shows that the diffusion-controlled liquid migration is dominant during the growth of β phase. Thus, the application of interrupted directional solidification should be further examined.

Peritectic Transformation and Primary Α-Dendrite Dissolution in Directionally Solidified Pb–26%Bi Alloy

Effect of Directional Solidification Methods on Solid Solution Window in Ni-based Single-Crystal Superalloy

Microstructure Formation in Pb-30wt.%Bi Peritectic Alloy

Microstructure Formation at Low Velocity During Directional Solidification of Pb-Bi Peritectic Alloys

Microstructure Formation During Unidirectionally Solidified Pb-Bi-Sn Tenary Quasi-Peritectic Alloy

Primary Dendrite Arm Spacing During Unidirectional Solidification of Pb–Bi Peritectic Alloys

Peritectic Reaction and Its Influences on the Microstructures Evolution During Directional Solidification of Fe–Ni Alloys

Effect of Sample Diameter on Primary and Secondary Dendrite Arm Spacings During Directional Solidification of Pb-26wt.%Bi Hypo-Peritectic Alloy

Phase and Microstructure Selection in Directional Solidification of Pb-Bi Peritectic Alloys

Investigation of the Non-Equilibrium Solidification and Microstructures of Al-Y Peritectic Alloys

Effect of Melt Convection on Primary Dendrite Arm Spacing in Directionally Solidified Pb-26%Bi Hypo-Peritectic Alloys

Phase and Microstructure Selection in Directionally Solidified Peritectic Alloys with Convection

Banding Structure Formation During Directional Solidification of Pb–Bi Peritectic Alloys

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Microstructure Evolution of Directionally Solidifi Ed Sn-16%Sb Hyperperitectic Alloy

Directional Solidification and Microstructure Selection for Ti-Al Peritectic Alloy

Local Melting/solidification During Peritectic Solidification in a Steep Temperature Gradient: Analysis of a Directionally Solidified Al–25at%Ni

Microsegregation of Peritectic Systems in a Temperature Gradient: Analysis in Directionally Solidified Sn–36at.%Ni Peritectic Alloy

Microstructure Evolution of Ti-(44-50)Al Alloys During Directional Peritectic Solidification

Liquid migration and peritectic transformation: Investigation on their contributions to growth of peritectic phase in interrupted directional solidification

A Lateral Remelting Phenomenon of the Primary Phase below the Temperature of Peritectic Reaction in Directionally Solidified Cu–Ge Alloys