Abstract:Dendrite growth velocity as a function of initial bulk undercooling was systematically studied in situ using high speed thermal imaging of highly undercooled Ni90Cu10 and Ni95Cu5 single phase alloy melts. For these two non-dilute concentrated alloys, the dendrite growth velocity first increased continuously at small and mediate undercooling regimes and then discontinuously to a maximum value at the high undercooling range. A clear plateau appeared in the growth velocity-undercooling curve revealed a gradual transition from mainly solute-controlled growth to mainly thermal-controlled growth, which was very similar to the solidification characteristics of a dilute alloy. The discontinuity appeared in the growth velocity-undercooling relationship was suggested to be induced by the finite solute diffusion speed in the bulk melt ahead of the advancing solid-liquid interface. Microstructure, substructure and microtexture of the two undercooled alloys were characterized using EBSD technique, and the fundamental mechanism behind “spontaneous grain refinement” is elucidated. The microstructure evolution indicated two kinds of grain refinements: one was dendrite remelting induced grain refinement and the other was recrystallization induced grain refinement. It was found that the texture of the as-solidified microstructure was getting more and more random as the initial bulk undercooling increased, which was due to the increased stress and recrystallization in the as-solidified microstructure. New evidence of grain refinement was found in the as-solidified samples. We found that the samples undercooled beyond the critical undercooling had a grain refined microstructure and that this corresponded with a clear discontinuity in the dendrite growth velocity-undercooling curve. Microstructural data suggested that in Ni-Cu alloys grain refinement at a high undercooling was a consequence of a recrystallization process, which contrasted with conventional grain refined alloys where grain refinement appeared to be the result of remelting-induced dendritic fragmentation.

Microstructure Formation During Unidirectionally Solidified Pb-Bi-Sn Tenary Quasi-Peritectic Alloy

Microstructure Formation in Pb-30wt.%Bi Peritectic Alloy

Microstructure Formation at Low Velocity During Directional Solidification of Pb-Bi Peritectic Alloys

Phase and Microstructure Selection in Directional Solidification of Pb-Bi Peritectic Alloys

Effect of Directional Solidification Methods on Solid Solution Window in Ni-based Single-Crystal Superalloy

Microstructure Evolution of Directionally Solidifi Ed Sn-16%Sb Hyperperitectic Alloy

Banding Structure Formation During Directional Solidification of Pb–Bi Peritectic Alloys

Peritectic Transformation and Primary Α-Dendrite Dissolution in Directionally Solidified Pb–26%Bi Alloy

Microstructure Evolution and Mechanical Properties of Sn0.7Cu0.7Bi Lead-Free Solders Produced by Directional Solidification

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Research on Lamellar Structure and Micro-Hardness of Directionally Solidified Sn-58bi Eutectic Alloy

Preparation and Microstructure Analysis of Continuous Unidirectional Solidification Cu–P–Sn Alloy

Observation of Dendrite Growth Velocity and Microstructure Transition in Highly Undercooled Single Phase Alloys

Primary Dendrite Arm Spacing During Unidirectional Solidification of Pb–Bi Peritectic Alloys

Phase Equilibria and Solidification of Ternary Sn–Bi–Ag Alloys

Phase-Field Modeling of Solute Trapping in Single-Phase Alloys During Directional Solidification

Rapid Solidification Structure Refinement Mechanism in Highly Undercooled Cu Based Ternary Alloys

Effect of Aging Treatment on Microstructural Evolution of Rapidly Solidified Eutectic Sn-Pb Alloy Powders

Deformation mechanism of various Sn-xBi alloys under tensile tests

Effect of Sample Diameter on Primary and Secondary Dendrite Arm Spacings During Directional Solidification of Pb-26wt.%Bi Hypo-Peritectic Alloy

Solidification behavior of Sn crystals − Under different temperature gradients