Precipitation behaviors and property variations of directionally solidified Cu-15Ni-8Sn alloy

Yufan Shi,Chengjun Guo,Xiangpeng Xiao,Yahui Gong,Hang Wang,Bin Yang
DOI: https://doi.org/10.1016/j.jallcom.2024.173945
IF: 6.2
2024-02-25
Journal of Alloys and Compounds
Abstract:The phase transformation process and its impact on the properties of directionally solidified Cu-15Ni-8Sn alloy have been comprehensively investigated. The results show that the phase transformation products during the aging process include the modulation structure, D0 22 ordered phase, L1 2 ordered phase, and ultimately the γ-D0 3 phase. The formation of modulation structure and D0 22 /L1 2 ordered phases plays a crucial role in improving the mechanical properties of the alloy. During the aging process, the mismatch between the D0 22 /L1 2 ordered phases and the matrix increases, resulting in larger coherent strains and further enhancing the mechanical properties. However, the formation of discontinuous precipitates can severely deteriorate the mechanical properties. These precipitates grow by consuming Ni/Sn atoms from both the ɑ'-matrix and D0 22 /L1 2 ordered phases, thereby disrupting the structure of the D0 22 /L1 2 ordered phases. By combining the Johnson-Mehl-Avrami-Kolmogorov and the Arrhenius equation, the kinetics of discontinuous precipitate formation during the aging process of directionally solidified Cu-15Ni-8Sn alloy were analyzed. The activation energy of discontinuous precipitates in directionally solidified Cu-15Ni-8Sn alloy is determined to be 225 kJ/mol. Significantly suppressing the formation of discontinuous precipitation is achieved through improvements in the preparation process.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?