Effects of cooling rate on microstructure and microhardness of directionally solidified Galvalume alloy
Ji-peng Li,De-gao Qiao,Jian Li,Xiao-yang Luo,Peng Peng,Xian-tao Yan,Xu-dong Zhang
DOI: https://doi.org/10.1007/s41230-024-3093-y
2024-02-10
China Foundry
Abstract:The influences of cooling rate on the phase constitution, microstructural length scale, and microhardness of directionally solidified Galvalume (Zn−55Al−1.6Si) alloy were investigated by directional solidification experiments at different withdrawal speeds (5, 10, 20, 50, 100, 200, and 400 μm·s −1 ). The results show that the microstructure of directionally solidified Galvalume alloys is composed of primary Al dendrites, Si-rich phase and (Zn−Al−Si) ternary eutectics at the withdrawal speed ranging from 5 to 400 μm·s −1 . As the withdrawal speed increases, the segregation of Si element intensifies, resulting in an increase in the area fraction of the Si-rich phase. In addition, the primary Al dendrites show significant refinement with an increase in the withdrawal speed. The relationship between the primary dendrite arm spacing ( λ 1 ) and the thermal parameters of solidification is obtained: λ 1 =127.3 V 0.31 . Moreover, as the withdrawal speed increases from 5 to 400 μm·s −1 , the microhardness of the alloy increases from 90 HV to 151 HV. This is a combined effect of grain refinement and second-phase strengthening.
metallurgy & metallurgical engineering