Abstract:The three-dimensional alpha-Mg dendritic morphology and branching mechanisms of directionally solidified Mg-Zn alloy were studied. Different microstructures were obtained under different pulling velocities various from 30 mu m/s to 70 mu m/s. Directional growth tissue of alpha-Mg dendrite was obseved in the specimen solidified under the pulling velocity of 30 mu m/s, while in the samples solifdified in other pulling velocities alpha-Mg dendrites tend to exhibit equiaxed morphologies without any directional growth structure. Coupled with a novel method X-ray synchrotron tomography and trational metallographic technique, the three-dimensional morphology and topology structure of the alpha-Mg in the sample with the pulling velocity of 30 mu m/s were characterized. The result show that the morphology of alpha-Mg dendrites are diversity and complicated in three-dimensional space. Through the analysis we demonstrated that the alpha-Mg dendrite grows with seven secondary dendrite arms around the trunk which is different from what have been observed in the directionally solidified AZ91([1][2]) and non-directional solidified Mg-Zn-[3] or Mg-Al-[4] alloys. In addition, the angles between the secondary dendrite arms and the trunck are different, with an angle of 53 similar to 54 degrees for three arms, 80 similar to 82 degrees for two and 60 degrees for the rest of the two arms. A hypothetical model of topological structure in alpha-Mg dendrites is proposed and the crystallography of the branches and advancing dendrite is discussed.

Three-Dimensional Dendritic Morphology and Branching Mechanism in Directionally Solidified Mg-Zn Alloy