Abstract:s Mullite whiskers were synthesized based on the S-L-S growth mechanism at high temperatures using nano-alumina sol and nano-silica sol as the main materials and ammonium molybdate tetrahydrate as an additive. The effects of the silica-aluminum ratio, addition of ammonium molybdate catalyst, sintering temperature, and sintering time on the generation of mullite whiskers were systematically investigated to determine the optimal synthesis conditions. It was shown that the best raw material formulation was (3Al 2 O 3 ·2.2SiO 2 ) 8 (MoO 3 ) 2 , which minimized the mass loss of precursor powder at 0–1200°C, with only 23.62%. The mullite whiskers generated by sintering for 1–3 h maintained good microforms without agglomeration. The optimal growth conditions were 1300°C sintering for 1 h. The resulting mullite whiskers grew along the [240] direction and had the largest aspect ratios up to 10.2–14.3. The highest generation rate was up to 94.5 wt% with a grain size of 81.6 nm. The BET surface area was 2.308 m 2 /g and the pore size was 5.44 nm. The mass loss at 0–1200°C was the least, only 1.32%, with good thermal stability. In addition, the effects of (xAl 2 O 3 ·ySiO 2 ) 8 (MoO 3 ) 2 (x:y=3:1.8, 3:2, 3:2.2) whiskers treated at 1300°C on the APSB adhesive and MSABS adhesive bonding were investigated in this paper, it was clear that whiskers with x:y=3:2.2 had the best enhancement effect. For APSB adhesive strength could be increased by up to 55% and the fracture displacement by 2.42 times. For MSABS adhesives, the strength could be increased by up to 47% and the fracture displacement by 1.49 times.

Effects of Synthesizing Temperature on Formation of Mullite Whiskers in Molten Sodium Sulfate Medium

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Preparation and Characterization of Mullite Whiskers from Different Silica Sources via Molten Salt Reaction

Molten Salt Synthesis of Mullite Whiskers from Silicon Carbide Precursor

Temperature feature on synthesizing mullite whiskers from coal fly ash and andalusite-sericite phyllite

Experimental Study of Synthesizing Mullite Whiskers by Andalusite-Sericite Phyllite

The effect of multiple factors on the synthesis of mullite whiskers based on the S-L-S mechanism and the comparison of strengthening performance

Molten salt synthesis of mullite whiskers from various alumina precursors

Analysis of Influencing Factors in the Preparation of Mullite Whiskers from Recovering Silicon-Rich Waste under Low-Temperature Conditions

Analysis of Factors Affecting the Preparation of Mullite Whiskers from Silica-Rich Slag and Application Studies

Effect of Heating Parameters on Sintering Behaviors and Properties of Mullite Whisker Frameworks

On the Synthesis and Dispersion of MuIIite Whiskers

Influence of Silica Sources on Morphology of Mullite Whiskers in Na2so4 Flux

Low-temperature Synthesis of Highly Porous Whisker-Structured Mullite Ceramic from Kaolin

MULLITE WHISKERS DERIVED FROM HIGH-ALUMINIUM COAL FLY ASH

Preparation of mullite whisker skeleton porous ceramic

The preparation of mullite foamed ceramics reinforced by in-situ SiC whiskers and their reinforcement mechanism

Synthesis of sillimanite whiskers

Preparation of Mullite Whiskers from Kaolin Via the Addition of Tribasic Calcium Phosphate

Formation mechanism of whiskers in Al–MgAl2O4–MgO refractories at 1400 °C under N2 atmosphere

Preparation of Mullite from Low-grade Kaolin