Electrolytic Deposition of Calcium Phosphate Coatings on Titanium Substrate

Liu Siqian,Lin Jun,Chen Yujuan,Qiu Jing,Weng Wenjian,Cheng Kui,Song Chenlu

2010-01-01

Rare Metal Materials and Engineering

Abstract:This study focuses on the influences of the electrolytic conditions on the crystal transformation of electrodeposited calcium phosphate coatings. In the experiment, Ti substrate was used. The electrolytic deposition was carried out in a diluted Ca(NO3)(2) and NH4H2PO4 solution with calcium ion concentration of 45 mmol/L and phosphate ion concentration of 25 mmol/L under different conditions such as temperature, deposition time and pH value. The deposited coatings were characterized by XRD and SEM. The results showed that temperature had the strongest impact on the phase transformation. The coating obtained at 37 degrees C had only DCPD phase. With increasing of temperature to 60 degrees C, the HA phase content in the coating increased. The deposition time did not show obvious affect on the phase of the coating. With pH value increased, both DCPD and OCP phase content increased, showing that high pH has both influences on phase growth and phase transformation. In the studied conditions, temperature was the most important parameter in phase transformation. Rising of deposition temperature could make calcium phosphate well transform to HA.