Abstract:A nano-hydroxyapatite coating on titanium substrate was directly prepared by electrochemical deposition method and was characterized by EDS, SEM, XRD and FTIR. It was observed that under a wide range of deposition conditions calcium-deficient hydroxyapatite coatings with different topographies can be prepared. Under a representative preparation condition, i.e. a titanium substrate was used as working electrode with a Pt electrode as counter electrode, the electrolyte was composed of 4.2 x 10(-4) mol (.) L-1 Ca(NO3)(2), 2.5 x 10(-4) mol (.) L-1 NaH2PO4 and 0.9% NaCl, with a pH adjusted to be 6.0, and galvanostatic mode with 1 mA (.) cm(-2) cathodic current density was applied at the temperature of 100 degreesC, a series of hydroxyapatite coatings under different deposition durations (15, 30, 60, 120 and 240 min) were prepared and characterized to investigate the coating growth behavior. Following laws of coating growth were observed: (1) preferential growth with the c-axis of the hydroxyapatite crystal perpendicular to working surface is always detected in the XRD measurements with the peak of (002) crystal face being greatly intensified; (2) the growth of grains at inner layer is impeded by the growth of those at cuter layer; when grains are packed closely, competition between the growths of grains at the same layer takes place; (3) the amount of deposited coating increases with deposition time while the chemical composition almost keeps the same.

Electrodeposition of Hydroxyapatite Coating on CoNiCrMo Substrate in Dilute Solution

Electrolytic Deposition of Hydroxyapatite Coating on CoNiCrMo Substrates

Preparation of hydroxyapatite coating on smooth implant surface by electrodeposition

Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate

Effect of EDTA on Electrodeposition of Hydroxyapatite Coatings

A Novel Method to Synthesize Hydroxyapatite Coating with Hierarchical Structure

Effect of Trisodium Citrate on Electrolytic Deposition of Hydroxyapatite Coatings

Synthesized Silicon-Substituted Hydroxyapatite Coating on Titanium Substrate by Electrochemical Deposition

Synthesis and Characterization of Zn-substituted Hydroxyapatite Coatings by Electrochemical Deposition

Effect of Supersaturation on the Morphology of Hydroxyapatite Crystals Deposited by Electrochemical Deposition on Titanium

Preparation of Hydroxyapatite Coatings on Enamel by Electrochemical Technique

Electrolytic Deposition of Calcium Phosphate Coatings on Titanium Substrate

The Crystal Growth Behavior of Hydroxyapatite Coating on Titanium Substrate under Electrochemical Deposition Conditions

Exploration of the electrochemical deposition of hydroxyapatite on HOPG

Preparation of Calcium Phosphate Coating on Pure Titanium Substrate by Electrodeposition Method

Study on Special Morphology Hydroxyapatite Bioactive Coating by Electrochemical Deposition

Deposition Kinetics of Apatite Coating on CVI Carbon/Carbon Composite by Sonoelectrodeposition Technique

A Study of the Process and Kinetics of Electrochemical Deposition and the Hydrothermal Synthesis of Hydroxyapatite Coatings

Recent advances in multifunctional hydroxyapatite coating by electrochemical deposition

Optimization of Process Parameters of Calcium Phosphate Coating on C/C Composites by Sonoelectrodeposition Technique

Preparation and Characterization of Hydroxyapatite Coatings on Human Enamel by Electrodeposition