Hydroxyapatite Coatings on Titanium Substrate Prepared by Hydrothermal-Electrochemical Deposition
du jing,he daihua,liu ping,liu xinkuan,ma fengcang,li wei,chen xiaohong,zhang ke,zhao jun
DOI: https://doi.org/10.11901/1005.3093.2016.143
2016-01-01
Abstract:Hydroxyapatite coatings were deposited on the Ti;Al;V surface by hydrothermal-electrochemical deposition method in an electrolyte composited of 0.025 mol/L Ca;, 0.015 mol/L H;PO;and0.1 mol/L NO;with addition of 2.5×10; mol/L Na-Citrate. The effect of the citrate and deposition time on the composition, microstructure, crystallinity and thickness of coatings as well as the bonding strength between the coating and the substrate were investigated. The results show that: in comparison with the electrolyte without citrate, HA coating formed in the electrolyte with addition of citrate exhibits uniform and compact appearance with smaller gain size, which covers entirely the substrate, correspondingly the bonding strength between the coating and the substrate increases from 15.39 MPa to 24.31 MPa. The thickness of HA coating increases non-linearly with deposition time. With the increase of deposition time,the orientation index of the（002） plane of HA increases first and then decreases, which reaching a maximum for 2 h deposition while the coating has much smaller grain size; the crystallinity and bonding strength of HA coatings all increase first, and then decrease, which come to peak values, ca 75.7% and24.3 MPa respectively by 2 h deposition.