Abstract:Bioceramic hydroxyapatite/sodium titanate coating on sandblasted titanium substrate was fabricated by a three-step process. At first, the sandblasted titanium substrate was coated with a flake-like sodium titanate layer by alkali-heat treatment. In the second step, the alkali-heat treated titanium substrate was hydrothermal treated at 180 °C for 4 h with calcium solutions. In the third step, the hydroxyapatite (HA) coating was deposited onto the hydrothermal treated layer via electrochemical deposition method. The surface topography and roughness of the coatings were determined by field emission scanning electron microscope (FESEM) and a mechanical contact profilometer, respectively. The surface compositions were evaluated by X-ray diffraction (XRD), energy-dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). The EDS, XPS, and XRD analysis confirm the presence of element Ca, Ca2+, and CaTiO3 on sodium titanate layer after hydrothermal treatment with Ca(NO3)2 solution, respectively. FESEM micrograph shows the rod/needle-shaped crystallites are highly densely packed on the calcium-ion-containing layer with an average size of ~50 nm in diameter. The results indicate that the sodium titanate layer containing Ca2+ ions possesses higher ability to induce HA formation compared with the pure sodium titanate layer. It is revealed that surface composition plays an important role in the electrochemical deposition of HA. The calcium-ion-containing layer probably makes the nucleation of HA easy and effectively promotes orientated growth of HA on flake-like sodium titanate surface. The sodium titanate layer possesses a lower corrosion current density and a higher corrosion potential than sandblasted-Ti substrate. The sodium titanate layer should act as a barrier to the release of metal ions from metallic substrate to physiological solutions and thus reducing the electrochemical reaction rate.

Controlled crystal growth of calcium phosphate on titanium surface by NaOH-treatment

Effect of Supersaturation on the Morphology of Hydroxyapatite Crystals Deposited by Electrochemical Deposition on Titanium

Morphologies of Hydroxyapatite Crystal Deposited on Titanium Surface with Electrochemical Technique

Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate

Ribbon-like and rod-like hydroxyapatite crystals deposited on titanium surface with electrochemical method

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

Influence of Solution Conditions on Deposition of Calcium Phosphate on Titanium by NaOH-treatment

Evolution of the magnesium incorporated amorphous calcium phosphate to nano-crystallized hydroxyapatite in alkaline solution

Oriented Growth of Phosphates on Polycrystalline Titanium in a Process Mimicking Biomineralization

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Carbonate apatite coating on titanium induced rapidly by precalcification.

Hydrothermal treatment of Ti surface to enhance the formation of low crystalline hydroxyl carbonate apatite

Calcium Phosphate Film Coating on Titanium Substrate by Electrochemical Deposition

Preparation of Layered Bioceramic Hydroxyapatite/Sodium Titanate Coatings on Titanium Substrates Using A Hybrid Technique of Alkali-Heat Treatment and Electrochemical Deposition

Mechanism of apatite formation on pure titanium treated with alkaline solution

Electrolytic Deposition of Calcium Phosphate Coatings on Titanium Substrate

Oriented Growth of Hydroxyapatite on (0001) Textured Titanium with Functionalized Self-Assembled Silane Monolayer As Template

Controlled Crystallization of Calcium-Phosphate under Stearic-Acid Monolayers

Hydrothermal growth of biomimetic calcium phosphate network structure on titanium surface for biomedical application

Ion beam treatment of titanium surfaces for enhancing deposition of hydroxyapatite from solution

Biomimetic Deposition of Hydroxyapatite by Mixed Acid Treatment of Titanium Surfaces