Abstract:Soaking time and loading rate are the two important process parameters for semi-solid powder forming, which are next only to powder temperature. However, there have been few investigations on the influence of soaking time and loading rate on the semi-solid compression of porous material, which is an effective method for studying the deformation characteristics of semi-solid materials and is widely used to optimize the semi-solid forming processes. Therefore, the microstructures, grain size and shape factor, liquid fraction, relative densities and stress–strain curves of Al-4Cu-Mg alloy with a porosity of 30% compacted at different soaking time and loading rates were measured, and the strain rate sensitivity coefficient, the relationship between peak stresses and strain rates, and the processing map were calculated and analyzed. The results indicate that as the soaking time increases, the particle grows and the liquid fraction increases slightly, and the liquid distribution changes from dots in grains to concentrating on grain boundaries in powders, making the relative density increase basically and the peak stress decrease firstly and then increase slowly. Thus, the most suitable soaking time for semi-solid compression is 2 to 5 min. With the loading rate increasing, the particle size reduces first and then increases, the relative density decreases, while the peak stress basically raises, combining the action of powder breakage, grain coarsening and liquid flowing. The peak stress basically has a power relationship with the strain rate, and the processing map can be used to analyze porous semi-solid materials, which are verified to be consistent with the experimental results. Therefore, the optimal semi-solid forming parameters of Al-4Cu-Mg alloy powders are at a deformation rate ranging from 0.6 to 6 mm/s and at a temperature of 860 to 873 K.

Research on Porous Superalloy Materials with Oriented Linear Porosity

Research on the structure and mechanical properties of Ni-Cr-Co-W-Mo-Al-Ti porous superalloy

Preparation and Properties of Porous Superalloy Materials with Hollow Spherical Pores

Preparation and Mechanical Properties of Oriented Porous GH3536

Preparation, Characterization and Designing of Porous Ti–6Al–4V Through Metal Injection Molding Without Space Holder

Effect of Al content on the microstructure and mechanical properties of the sintered Fe–Mn–Al porous steel

Preparation of Controllable Porous Ti–Al Materials with Zn Space Holders

Fabricating of Open-Cell Porous Al-Si Alloy with Pressure Penetration Casting

Effect of Pressure and Temperature on Densification in Electric Field-Assisted Sintering of Inconel 718 Superalloy

Pore/skeleton structure and compressive strength of porous Mo3Si-Mo5Si3-Mo5SiB2 intermetallic compounds prepared by spark plasma sintering and homogenization treatment

Pore Structure and Compression Behavior of Porous TiAl Alloys by Freeze Casting

Microstructures and Properties of Porous TiAl-based Intermetallics Prepared by Freeze-Casting

Preliminary development of porous aluminum via powder metallurgy technique

Influence of Soaking Time and Loading Rate on Semi-solid Compression of Porous Al-4Cu-Mg Alloy

Fabrication of Porous SiAlON Using Fe2O3 As Pore Former

Correlation between pore structure and compression behavior of porous sintered Cu-Ni-Cr alloy at elevated temperatures

Effects of preparation process on microstructure and properties of porous Ti6Al4V

Study of fabricating technology of a porous aluminum alloy

Fabrication of Porous Aluminum with Controllable Open-Pore Fraction

Effects of Microporosity and Precipitates on the Cracking Behavior in Polycrystalline Superalloy Inconel 718

Effect of Mechanical Alloying and Sintering Environment on the Crystallographic Evolution, Microstructure, Mechanical and Corrosion Properties of Porous Ti4Al4Co Alloy