Fabrication of Porous SiAlON Using Fe2O3 As Pore Former

Qing Wen Duan,Rong Zhen Liu,Hai Yun Jin,Jian Feng Yang,Zhi Hao Jin
DOI: https://doi.org/10.4028/www.scientific.net/msf.804.267
2014-01-01
Materials Science Forum
Abstract:Porous SiAlON ceramics were fabricated by carbo-thermal reduction nitridation method using Fe2O3 as pore former. Particle size effects of Fe2O3 were reported in this paper. The results showed that composites were composed by SiAlON, AlN and Iron Silicon phases. The median pore diameter of Sialon was affected by the composition and particle size of Fe2O3. The fracture mode of this material was intergranular. With the increase of Fe2O3 additions, the porosity of this materials increased. The bending strength of this material was reversely proportional to Fe2O3 particle size. The maximum bending strength of Porous materials with 30wt.% Fe2O3 additions (with a porosity about 65% and the pore size is about 1μm) could reach 22 MPa. The porous Sialon ceramics with a smaller pore size exhibited a higher bending strength.
What problem does this paper attempt to address?