Abstract:Owing to their unique microstructure, GH3230 superalloys prepared using laser powder bed fusion (LPBF) exhibit high strength but low ductility, which limits their functional performance in engine combustion chambers. In this study, the process parameters were optimized to obtain LPBF GH3230 with minimal defects, and solid-solution treatment (ST) was conducted to modulate its inhomogeneous microstructure and mechanical properties. The results revealed that ST eliminated the substructure of as-printed (AP) samples and transformed nano-M 23 C 6 into micron and submicron M 6 C/M 12 C in situ. Significant amounts of M 6 C/M 12 C promoted Orowan strengthening, but the quasi-continuous semi-coherent lattice interface between M 6 C/M 12 C and the matrix was a weak zone for cracking, resulting in reduced plasticity owing to the presence of micron carbide. The increased solid solution temperature causes the carbide to remelt, triggering a strong plastic transformation. The impact of carbide size on strength and plasticity conversion rate was more significant than that of carbide content. Final, LPBF-GH3230 samples containing micron carbides were obtained in ST below 1230 °C with an ultimate tensile strength (UTS) comparable to that of forgings. Further increase in the ST temperature to 1280 °C eliminated the carbides, a LPBF-GH3230 that fulfilled the strength standard for cast parts (647 ± 23 MPa) with an excellent elongation (39.4 ± 1.7%) was obtained. This study provides a theoretical basis for the practical application of the LPBF GH3230 superalloy in the aerospace industry and offers guidance for improving post-treatment methods to ensure high plasticity.

Preparation and Mechanical Properties of Oriented Porous GH3536

Mechanical Properties and Fracture Behavior of Laser Powder-Bed-Fused GH3536 Superalloy

Research on Porous Superalloy Materials with Oriented Linear Porosity

Preparation and Properties of Porous Superalloy Materials with Hollow Spherical Pores

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Microstructures and Properties of Porous TiAl-based Intermetallics Prepared by Freeze-Casting

Fabrication of Porous Alumina Ceramics with Directional Pore Channels Structure by Freeze-Gel Casting Processing

Preparation and properties of porous alumina ceramics with oriented cylindrical pores produced by an extrusion method

Towards Homogeneous Distribution of Coarse Grain in a Tri-Modal Al-based Composites Utilizing Localized Grain Growth

Nickel base superalloy GH4049 prepared by powder metallurgy

Research on the structure and mechanical properties of Ni-Cr-Co-W-Mo-Al-Ti porous superalloy

GH3536 Superalloy Prepared by Selective Laser Melting: Microstructure and Properties

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

Identification of Precipitates in the As-cast Microstructure and Its Dissolution Behavior During Homogenization of Difficult-to-Deform GH4141 Superalloy

Strength-plasticity transition mechanism after the solution treatment of GH3230 superalloy fabricated via laser powder bed fusion

Study on the Fabrication of Porous TiAl Alloy Via Non-Aqueous Gel Casting of a TiH2 and Al Powder Mixture

Oxidation kinetic behavior and microstructure mechanism of GH3536 alloy fabricated by laser powder bed fusion

Pore Architectures and Mechanical Properties of Porous α-SiAlON Ceramics Fabricated via Unidirectional Freeze Casting Based on Camphene-Templating

Preparation and performance study of POE-g-MAH/GMA toughened bio-based PA56 alloys

Structural, Mechanical, and Tribological Properties of Oriented Ultra-High Molecular Weight Polyethylene/Graphene Nanoplates/Polyaniline Films

Laser powder bed fusion of GH3536 nickel-based superalloys: Processing parameters, microstructure and mechanical properties