Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Effects of Microporosity and Precipitates on the Cracking Behavior in Polycrystalline Superalloy Inconel 718

Fracture Mechanisms Induced by Microporosity and Precipitates in Isothermal Fatigue of Polycrystalline Nickel Based Superalloy

Analysis of Microporosity-Dependent Fatigue Crack Behavior in Alloy 718 by Using Synchronic Radiation X-Ray CT and FEM

Crack formation and microstructure-sensitive propagation in low cycle fatigue of a polycrystalline nickel-based superalloy with different heat treatments

Yttrium Induced Formation of New Pores in an As-Cast Nickel-Based Single Crystal Superalloy

Growth of Casting Microcrack and Micropore in Single-Crystal Superalloys Analysed by Three-Dimensional Unit Cell

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

The Influence of Grain Boundary Angle on the Hot Cracking of Single Crystal Superalloy DD6

Casting Microporosity Growth in Single-Crystal Superalloys by A Three-Dimensional Unit Cell Analysis

Casting Microporosity Growth Simulation in Single-Crystal Superalloys

Microstructural insights into fatigue short crack propagation resistance and rate fluctuation in a Ni-based superalloy manufactured by Laser powder bed fusion

Causes Analysis on Cracks in Nickel-Based Single Crystal Superalloy Fabricated by Laser Powder Deposition Additive Manufacturing

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Effect of crack on morphology evolution of the precipitates in Nickel-based superalloys under applied stress

Effect of Solidification Behavior on Microstructures and Mechanical Properties of Ni-Cr-Fe Superalloy Investment Casting

In-situ X-ray tomography investigation of pore damage effects during a tensile test of a Ni-based single crystal superalloy

Crack Inhibition and Performance Modification of NiCoCr-Based Superalloy with Y2O3 Nanoparticles by Laser Metal Deposition

Investigation on the Microporosity Formation of IN718 Alloy during Laser Cladding Based on Cellular Automaton

Crack Inhibition and Crystallographic Texture Control in an Additively Manufactured IN738LC Ni-based Superalloy

Statistical Study of Ductility-Dip Cracking Induced Plastic Deformation in Polycrystalline Laser 3d Printed Ni-Based Superalloy

Research on the influence of microstructure on the initiation and propagation of micro-cracks of superalloy GH4169