Abstract:The mechanical properties of nickel-based single crystal superalloys deteriorate with increasing misorientation, thus the finished product rate of the casting of single crystal turbine airfoils may be reduced due to the formation of grain boundaries especially when the misorientation angle exceeds to some extent. To this day, evolution of the microstructures at the grain boundaries with misorientation and the relationship between the microstructures and the mechanical properties are still unclear. In this work a detailed characterization of the misorientation related microstructure at the grain boundary in DD6 single crystal superalloy has been carried out using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques; the elemental distribution at the grain boundaries has been analyzed by energy dispersive (EDS) X-ray mapping; and the effect of precipitation of μ phases at the grain boundary on the mechanical property has been evaluated by finite element calculation. It is shown that the proportion of γ phase at the grain boundaries decreases, while the proportion of γ′ phase at the grain boundaries increases with increasing misorientation; the μ phase is precipitated at the grain boundaries when the misorientation angle exceeds about 10° and thus it could lead to a dramatic deterioration of the mechanical properties, as well as that the enrichment of Re and W gradually disappears as the misorientation angle increases. All these factors may result in the degradation of the mechanical properties at the grain boundaries as the misorientation increases. Furthermore, the finite element calculation confirms that precipitation of μ phases at the grain boundary is responsible for the significant deterioration of the mechanical properties when the misorientation exceeds about 10°. This work provides a physical imaging of the microstructure for understanding the relationship between the mechanical properties and the misorientation of the grain boundaries in the single crystal superalloy. Based on our study we hope that we can offer some scientific basis for further improvement of the nickel-based single crystal superalloys.

The Influence of Grain Boundary Angle on the Hot Cracking of Single Crystal Superalloy DD6

Hot cracking behavior and mechanism of a third-generation Ni-based single-crystal superalloy during directed energy deposition

Mechanism of Grain Boundary Angle on Solidification Cracking in Directed Energy Deposition Hastelloy X Superalloys

Transient Thermal Fatigue Crack Propagation Behavior of a Nickel-Based Single-Crystal Superalloy

Effects of Low- to Medium-Angle Grain Boundaries on Creep Properties of Superalloy

Microscopic Damage and Fracture Mechanism of Nickel-based Single Crystal Superalloy during Low Cycle Fatigue at Elevated Temperature

Effect of Grain Boundary Behaviour on Ductility Dip Cracking Mechanism

Effect of grain boundary's state on the hot cracking tendency of directionally solidified Al-Cu and Rene 125 alloys

Atomic-scale grain boundary engineering to overcome hot-cracking in additively-manufactured superalloys

Misorientation Related Microstructure at the Grain Boundary in A Nickel-Based Single Crystal Superalloy

Effect of Carbides and Γ/γ' Eutectic on Crack Initiation and Propagation in Ni-based Superalloy

Formation Mechanisms of Hot Cracks in Laser Additive Repairing Single Crystal Superalloys

Hot cracking behavior and mechanism of the IC10 directionally solidified superalloy during laser re-melting

Investigation on the grain boundary strengthening effect of a nickel‐based superalloy

Effects of crack-γ/γ' interface relative distributions on the deformation and crack growth behaviors of a nickel-based superalloy

A Quantitative Approach to Investigate Discontinuous Precipitation on Grain Boundary of Ni-Based Single Crystal Superalloys

Misorientation effect of grain boundary on the formation of discontinuous precipitation in second and third generation single crystal superalloys

Fine grained microstructure crystallographic feature and its effect on mechanical behavior in Ni–Cr–W superalloy

Recrystallization Mechanism of Typical Ni-based Superalloys

Hot Cracking Susceptibility Prediction from Quantitative Multi-Phase Field Simulations with Grain Boundary Effects

Damage Tolerance of Low Angle Grain Boundary in a Fourth Generation Nickel-based Single Crystal Superalloy at 1100 °C Service Conditions