Abstract:The Ni-Fe-based superalloy GH4169 (Inconel718) is widely used for several critical gas-turbine components which are hot forged. Its microstructure and property are sensitive to the parameter adjustment during hot working process. To obtain required low-cycle fatigue and fracture properties, it is essential that the microstructure is controlled during preheating and heat treatment. The evolution of non-uniform microstructure during hot working is more complicated than that of uniform microstructure. On the other hand, various secondary phases can be observed in GH4169 alloy, thus it is important to investigate the effect of secondary phases on the microstructure evolution during forging process. In this work, the mechanisms of non-uniform microstructure evolution in GH4169 alloy were studied by analyzing the evolution of secondary phases, grain boundary misorientation, grain size and interactions of dislocation. It is found that the volume fraction of 8 phase increases with the increasing of temperature and heating time at the lower temperature. While at the higher temperature, it decreases monotonously with the temperature increasing, but increases first and then decreases to stable value with time increasing. The pinning effect of secondary phases in GH4169 alloy can be concluded that the gamma '' phase and 8 phase precipitated within the grains retain movement of dislocation, the 8 phase precipitated at the grain boundary hinders the nucleation and growth of recrystallized grains, and the carbides limits the grain growth. The frequency of low angle grain boundary decreases with temperature and time increasing, and the mobility of low angle grain boundary increases with temperature increasing. The uniformity of microstructure and the size of equaxied subgrain increases with heating temperature and time increasing. Continuous recrystallization of elongated grain occurs at specific conditions. The mechanisms of non-uniform microstructure evolution during heating process can be concluded as sub grain growth, recrystallized grain growth, and anneal twinning nucleation and growth. The recrystallized grains are formed by the growth of subgrains conducted by the rotation of low angle grain boundary and the movement of dislocation. When the grain growth is pinned, the mechanisms for the energy dissipation is the nucleation and growth of anneal twinning. And the growth of anneal twinning promotes the generation of low angle grain boundaries at the tip of partial anneal twinning.

Research on the influence of microstructure on the initiation and propagation of micro-cracks of superalloy GH4169

Fractograph examination of superalloy GH4169 at low cycle fatigue

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

Investigation of small fatigue crack initiation and growth behaviour of nickel base superalloy GH4169

A Study on Influence of Microstructure on Crack Propagation of GH864 Alloy

Micro-notch Size Effect on Small Fatigue Crack Propagation of Nickel-Based Superalloy GH4169

Numerical simulation on creep damage and crack initiation behaviour of nickel-based single crystal superalloys containing a casting void

Microstructural insights into fatigue short crack propagation resistance and rate fluctuation in a Ni-based superalloy manufactured by Laser powder bed fusion

Investigation on Microstructure Evolution and Fracture Morphology of Single Crystal Nickel-Base Superalloys under Creep-Fatigue Interaction Loading

Grain Size Effect on the Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169

Mechanisms of Non-Uniform Microstructure Evolution in Gh4169 Alloy During Heating Process

Investigations of micro-notch effect on small fatigue crack initiation behaviour in nickel-based alloy GH4169: Experiments and simulations

Propagation Behaviors of Small Cracks in Powder Metallurgy Nickel-Based Superalloy FGH4096

The Influence of Grain Boundary Angle on the Hot Cracking of Single Crystal Superalloy DD6

Influence of Notch on Creep Properties of GH3536 Nickel-Based Superalloy

Creep Damage Mechanism and Γ′-Phase Morphology of a V-notched Round Bar in Ni-based Single Crystal Superalloys

Research on crack propagation behaviour of nickel-based superalloy under thermal shock load

Effect of Micron-Sized Particles on the Crack Growth Behavior of a Ni-based Powder Metallurgy Superalloy

Influence of Grain Size on the Small Fatigue Crack Initiation and Propagation Behaviors of a Nickel-Based Superalloy at 650 °C

Crack formation and microstructure-sensitive propagation in low cycle fatigue of a polycrystalline nickel-based superalloy with different heat treatments

Crack Characteristics Analysis and Mechanisms in GH3536 Alloy Manufactured by Laser Powder Bed Fusion