Abstract:Amorphous Fe73.5-xCoxSi13.5B9Cu1Nb3（x=10,30,50） ribbons were prepared by the single copper wheel melt spinning technique in the air atmosphere.The nanocrystallization kinetics of amorphous ribbons was investigated by differential scanning calorimetry（DSC）.The apparent activation energies of amorphous ribbons were calculated by using Kissinger and Ozawa methods.It was found that the activation energies of the first crystallization reduce and those of the second crystallization rise with increasing Co content.The local Avrami parameter m for primary crystallization was calculated using Johnson-Mehl-Avrami（JMA） model.The values of the Avrami parameter showed that the primary crystallization mechanism of amorphous ribbons varied at different stages.In the initial stage,the crystallization mechanism was bulk crystallization with three dimensional nucleation and grain growth controlled by diffusion.In the following stage,it was surface crystallization with one dimensional nucleation and grain growth at a near zero nucleation rate.The variation of soft magnetic properties of nanocrystalline Fe63.5Co10Si13.5B9Cu1Nb3 powder cores as a function of milling time has been investigated.It was found that the effective permeability of the cores shows high frequency stability and decreases with increasing milling time.The quality factor increases with increasing frequency in the lower frequency range,reaches a maximum at the frequency of 80 kHz,and then decreases gradually with increasing frequency.

Effect of Crystallization Quality on Ferromagnetism in Zn1 − Xcoxo Nanopowders

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Preparation and Magnetic Properties of Zn–Cu–Cr–Sm Ferrite Via a Rheological Phase Reaction Method

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

Synthesis of 1d and Heavily Doped Zn1-Xcoxo Six-Prism Nanorods: Improvement of Blue-Green Emission and Room Temperature Ferromagnetism

Exciton quenching and ferromagnetism-to-ferrimagnetism crossover in diluted magnetic semiconducting Zn1-xCoxO nanogranular nanofibers

Effect of Zn Substitution on Morphology and Magnetic Properties of Cufe2o4 Nanofibers

Room-Temperature Ferromagnetism in Co-Doped Zno Fabricated by Coprecipitation Method

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Effects of Nd and Co on thermal stability of nanocomposite Nd2Fe14B/a-Fe magnets

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

Signature Of Intrinsic High-Temperature Ferromagnetism In Cobalt-Doped Zinc Oxide Nanocrystals

Effect Of Oxygen Deficiency On Room Temperature Ferromagnetism In Co Doped Zno

Synthesis And Magnetic Properties Of Zn1-Xcoxo Nanorods

Synthesis and influence of Zn substitution on optical and magnetic properties of cobalt ferrite nanoparticles by a polyacrylamide gel route

Synthesis of Co‐Doped ZnO Nanofibers and Their Magnetic Properties

Structure phase transition and magnetic properties of nanocrystalline

Effect of Zn-substitution on magnetic structure of cobalt ferrite nanoparticles

High-temperature Ferromagnetism in Cobalt-Doped ZnO Single-Crystalline Nanorods

Magnetism of Zno Nanoparticles: Dependence on Crystallite Size and Surfactant Coating

The Structural and Magnetic Properties For Zn1-xCoxO Thin Films