Abstract:Titanium carbide powders were synthesized under an argon atmosphere using titanium dioxide and pyrolysis carbon derived from pyrolyzed phenolic resin as raw materials. The effects of synthesis temperature, holding time, and C/Ti molar ratio on the phase composition and morphology of the synthesized powders were investigated. The results show that the pyrolyzed phenolic resin at 1000 degrees C is a carbon source composed of amorphous and crystalline carbon. Increasing the C/Ti molar ratio of the mixed powder can reduce the content of titanium oxide impurity, indicating the improvement in the purity of TiC powder. In addition, the C/Ti molar ratio can also significantly affect the morphology of the synthesized TiC powders. SEM and EDS results exhibit that the atomic content on the surface of TiC particles is closely correlated with the atomic distribution on the surface of the particles. TiC powder with a median particle size of 384 nm could be synthesized at 1500 degrees C for 30 min at the C/ Ti molar ratio of 2.3:1. In addition, the sinterability of the synthesized TiC powder was preliminarily discussed. The hardness and fracture toughness of the TiC ceramic sintered at 2000 degrees C under 40 MPa with a dwell time of 2 h are 15.92 GPa and 3.22 MPam 1/2 , respectively.

Ti3SiC2 Powder Synthesis

Facile Synthesis of Ti3SiC2 Powder by High Energy Ball-Milling and Vacuum Pressureless Heat-Treating Process from Ti–TiC–SiC–Al Powder Mixtures

Reaction Synthesis of Ti3SiC2 from Mixture of Elemental Powders

A Study on Formation of Ti3sic2 Synthesized by Elemental Powders

Preparation and characterization of Ti3SiC2 powder

Effect of Sn and Si on the Synthesis of Ti<sub>3</sub>Al(Sn/Si)C<sub>2</sub> by Self-Propagating High-Temperature Sintering

Phase Assembly of Ti2SnC Powders

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Synthesis of High-Purity Ti3SiC2 Polycrystals by Hot-Pressing of the Elemental Powders

Reaction Mechanism of Ti<SUB>3</SUB>SiC<SUB>2</SUB> Formed on the Diamond

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Reaction mechanism of Ti3SiC2 formed on the diamond

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Synthesis of Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials with B<sub>2</sub>O<sub>3</sub> Additive

Phase Assembly of Ti<sub>2</sub>SnC Powders

Synthesis of Ti3sic2 by Pressureless Sintering of the Elemental Powders in Vacuum

Synthesis of Ti3SiC2 Bulk Materials with B2O3 Additive

Synthesis of high pure Ti3AlC2 and Ti2AlC powders from TiH2 powders as Ti source by tube furnace

Synthesis of Ti3AlC2 Powder by High Energy Ball Milling and High Temperature Heat Treatment

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction