Abstract:This study deals with the effect of conventional sintering and microwave sintering on the densification kinetics of Titanium Carbide (TiC) in the presence of Ni (1, 1.5, 2 wt%). TiC compacts were obtained after uniaxial pressing of powders synthesised by ball milling of Titanium and Carbon and sintering was done in the presence of Nickel. The samples prepared were subjected to conventional as well as microwave sintering. The XRD and SEM analysis were used for a study of the reaction of Ti and C powders upon addition of Ni, which reduced the sintering temperature to 1200 °C. The densification of TiC powders was due to the Ti-Ni eutectic system, the liquid phase formed at this temperature assisting the sintering process. The SEM images revealed the flake like structure of TiC in which the carbon diffused into Ti upon the addition of Ni, thereby supporting enhanced mass transfer. The XRD pattern showed the presence of Titanium Oxide (TiO2) along with TiC which resulted in non-uniform distribution of hardness. Maximum hardness was achieved in the conventional sintered compacts which gradually increased with increase in Ni addition. The presence of the oxide phase and the formation of micro cracks resulted in non-uniform hardness for microwave sintered compacts. The maximum hardness of conventional sintered compact (375 HLD) was nearly 1.5 times more than the maximum hardness of the microwave sintered compact (250 HLD). The density of the microwave sintered compact was found to be higher by 8% than with the conventionally sintered compact.

Facile Synthesis of Ti3SiC2 Powder by High Energy Ball-Milling and Vacuum Pressureless Heat-Treating Process from Ti–TiC–SiC–Al Powder Mixtures

Synthesis Of High-Purity Powder Ti3alc2 Materials By Pressureless Sintering

Synthesis of Ti3SiC2 Powder by Mechanical Alloying and Mechanical Property of the Sintered Compacts.

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Synthesis of Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials with B<sub>2</sub>O<sub>3</sub> Additive

Synthesis of High Purity Ti3AlC2 Bulk Material by Hot-Pressing

Synthesis of High-Purity Ti3SiC2 Polycrystals by Hot-Pressing of the Elemental Powders

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Synthesis of Ti3SiC2 Bulk Materials with B2O3 Additive

Synthesis of fine grain Ti3SiC2 by spark plasma sintering with additive of aluminum

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Fabrication of high purity Ti3SiC2 from Ti/Si/C with the aids of Al by spark plasma sintering

Synthesis of high pure Ti3AlC2 and Ti2AlC powders from TiH2 powders as Ti source by tube furnace

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Effect of Sn and Si on the Synthesis of Ti<sub>3</sub>Al(Sn/Si)C<sub>2</sub> by Self-Propagating High-Temperature Sintering

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Reaction Synthesis of Ti3SiC2 from Mixture of Elemental Powders

Fabrication of Ti3AlC2 Powder with High-Purity by Pressureless Sintering

Fabrication and Mechanical Properties of High-Pure Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials Directly by Hot-Pressing its Powder

Facile Synthesis of Ti3SiC2 Powder by High Energy Ball-Milling and Vacuum Pressureless Heat-Treating Process from Ti–TiC–SiC–Al Powder Mixtures

Synthesis Of High-Purity Powder Ti3alc2 Materials By Pressureless Sintering

Synthesis of Ti3SiC2 Powder by Mechanical Alloying and Mechanical Property of the Sintered Compacts.

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Synthesis of Ti&lt;sub&gt;3&lt;/sub&gt;SiC&lt;sub&gt;2&lt;/sub&gt; Bulk Materials with B&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt; Additive

Synthesis of High Purity Ti3AlC2 Bulk Material by Hot-Pressing

Synthesis of High-Purity Ti3SiC2 Polycrystals by Hot-Pressing of the Elemental Powders

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Synthesis of Ti3SiC2 Bulk Materials with B2O3 Additive

Synthesis of fine grain Ti3SiC2 by spark plasma sintering with additive of aluminum

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Fabrication of high purity Ti3SiC2 from Ti/Si/C with the aids of Al by spark plasma sintering

Synthesis of high pure Ti3AlC2 and Ti2AlC powders from TiH2 powders as Ti source by tube furnace

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Effect of Sn and Si on the Synthesis of Ti<sub>3</sub>Al(Sn/Si)C<sub>2</sub> by Self-Propagating High-Temperature Sintering

Fabrication of Ti&lt;sub&gt;3&lt;/sub&gt;AlC&lt;sub&gt;2&lt;/sub&gt; Powder with High-Purity by Pressureless Sintering

Reaction Synthesis of Ti3SiC2 from Mixture of Elemental Powders

Fabrication of Ti3AlC2 Powder with High-Purity by Pressureless Sintering

Fabrication and Mechanical Properties of High-Pure Ti&lt;sub&gt;3&lt;/sub&gt;SiC&lt;sub&gt;2&lt;/sub&gt; Bulk Materials Directly by Hot-Pressing its Powder

Synthesis of Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials with B<sub>2</sub>O<sub>3</sub> Additive

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Fabrication and Mechanical Properties of High-Pure Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials Directly by Hot-Pressing its Powder