Abstract:A major remaining challenge for Nb3Sn high field magnets is their training due to random temperature variations in the coils. The main objective of our research is to reduce or eliminate it by finding novel impregnation materials in replacement of the epoxies currently used. An organic olefin-based thermosetting dicyclopentadiene (DCP) resin, C10H12, commercially available in Japan as TELENE® by RIMTEC, was used to impregnate a short Nb3Sn undulator coil developed by ANL and FNAL. This magnet reached short sample limit after only two quenches, compared with ~100 when CTD-101K® was used. Ductility, i.e. the ability to accept large strains, and toughness were identified as key properties to achieve these results. In addition, we have been investigating whether mixing TELENE with high heat capacity ceramic powders such as Gd2O3, Gd2O2S, and HoCu2, increases the specific heat (Cp) of impregnated Nb3Sn superconducting magnets. The viscosity, heat capacity, thermal conductivity, and other physical properties of TELENE with high-Cp powder fillers were measured in this study as a function of temperature and magnetic field. The TELENE-87wt%Gd2O2S had a peak in Cp between 4.3 K and 5.3 K at fields between 0 and 8 T. We have also investigated the effect on the mechanical properties of pure and mixed TELENE under 10 Gy of gamma ray irradiation at the Takasaki Advanced Radiation Research Institute in Takasaki, Japan. TELENE-87wt%Gd2O2S exhibited exceptional radiation resistance. Impregnating an undulator coil with TELENE mixed with Gd2O2S powder will verify whether the coils' thermal stability further improves, or whether its low diffusivity will require engineering the material with high-thermal conductivity components. Short magnet training will lead to better magnet reliability, lower magnet margins, lower risk and substantial saving in accelerators' commissioning costs.

Training performance of Nb3Sn Rutherford cables in a channel with a wide range of impregnation materials

Improved training in paraffin-wax impregnated Nb3Sn Rutherford cables demonstrated in BOX samples

Training-free demonstration of a 5.4 T Nb 3 Sn canted-cosine-theta accelerator dipole impregnated with paraffin wax

Assessment of Training Performance, Degradation and Robustness of Paraffin-Wax Impregnated Nb 3 Sn Demonstrator under High Magnetic Field

Minimum Quench Energy Of Nb$_3$Sn Wires With High Specific Heat Tape

A new ductile, tougher resin for impregnation of superconducting magnets

AC Loss and Contact Resistance In Copper-Stabilized Nb3Al Rutherford Cables with and without a Stainless Steel Core

Commissioning, Performance, and Effect of the Quench Current-boosting Device on a Dedicated Superconducting Magnet

Nb3Sn wire shape and cross sectional area inhomogeneity in Rutherford cables

Deformation Behavior and Degradation on Rutherford Cabling of Nb 3 Sn Wires

Test samples and infrastructure for accelerator magnet developments

Determination of the electromechanical limits of high-performance Nb$_3$Sn Rutherford cables under transverse stress from a single-wire experiment

A Combined Testing and Modelling Methodology for the Mechanics of High-Field Superconducting Magnets

Fracture Toughness, Radiation Hardness, and Processibility of Polymers for Superconducting Magnets

Performance of a MQXF Nb3Sn Quadrupole Magnet Under Different Stress Level

A Novel Aluminum-Stabilized Stacked REBCO Tape Cable

Effect of CLIQ on training of HL-LHC quadrupole magnets

Design and analysis of a HTS internally cooled cable for the Muon Collider target and capture solenoid magnets

Research on Insulation Technology for Nb3Sn Layer Coil of Superconducting Conductor Testing Facility

First Results from Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System