Competitive correlation between the interface layers determines the shear strength in Kovar/AgCuTi/Si3N4 joints

Haifeng Xu,Jie Wang,Fengsong Fan,Zepeng Zhang,Deyin Zhang,Haoyang Wu,Zhirui Zhang,Aimin Chu,Baorui Jia,Enxiang Pu,Xuanhui Qu,Mingli Qin

DOI: https://doi.org/10.1111/ijac.14920

2024-10-12

International Journal of Applied Ceramic Technology

Abstract:⟡ Ti‐rich layers of Fe, Co, and Ni elements can be found at the interface of Kovar/AgCuTi. ⟡ Shear strength in Kovar/AgCuTi/Si3N4 joints is contingent upon the competitive correlation between Kovar/AgCuTi and AgCuTi/Si3N4 interface layers. ⟡ By adjusting the interface reaction layers' thicknesses, the prepared Kovar/AgCuTi/Si3N4 joints reach a high shear strength of 154.3 MPa. ⟡ Interface fracture mechanism was explained using first principles that the Ag (111)/Fe2Ti (001) interface has stronger bonding than the Ag (111)/Ti5Si3 (001) interface. As a promising high‐thermal‐conductivity ceramics, the direct bonding of Si3N4 with metals remains challenging. Here, we employed active metal brazing of Si3N4 ceramics and Kovar alloys using AgCuTi metal filler, and found that the shear strength in the prepared Kovar/AgCuTi/Si3N4 joints depends on the competitive correlation between the interface layers. The competitive consumption for active element Ti by Kovar/AgCuTi interfacial reactions reduced AgCuTi/Si3N4 interface layer thickness and deteriorated final shear strength, even when using a high‐Ti‐content filler. Surface analysis indicated that interfacial fracture between Ag‐based solid solution and Ti5Si3 was the primary cause of failure. Density functional theory (DFT) revealed that Ag (111)/Fe2Ti (001) interface had higher ideal work of adhesion (Wad) than Ag (111)/Ti5Si3 (001) interface, confirming the importance of AgCuTi/Si3N4 interface layer. Ultimately, by adjusting interface reaction layer thickness, the joints reached a high shear strength of 154.3 MPa.

materials science, ceramics