Abstract:C/C composite was brazed to TiAl intermetallic compound using a commercial BNi-2 brazing filler metal under vacuum brazing condition. The brazing temperature was 1030~1150 °C and the holding time was 20 min. The joint interfacial microstructures and mechanical properties were studied, and the fracture behavior and joining mechanism were also investigated. The effect of brazing temperature on the joint shear strength was explored. The results showed that a perfect interface joint can be obtained by using BNi-2 to braze C/C and TiAl. During brazing, Ti, Cr, and other carbide forming elements diffused to C/C composite side, forming Cr3C2, Cr7C3, TiC, and other carbides, and realizing metallurgical joining between the brazing filler metal and C/C composite. The microstructure of the interface of C/C composite and TiAl intermetallic compound joint is as follows: TiAl alloy → TiAl + AlNi3 → AlNi2Ti → Ni(s, s) + Ti3Al + Ni3Si → Ni(s, s) + Ni3(Si, B) + CrB → Ni(s, s) + Ni3Si + TiCr2 → (Ti, Cr)C → C/C composite. When the holding time is fixed, with the increase of brazing temperature, the shear strength of the joint increases first and then decreases. The maximum average room temperature shear strength of the brazed joint was 11.62 MPa, while the brazing temperature was 1060 °C and the holding time was 20 min.

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Brazing of C/C Composite to TiAl Alloy Using (ti/ni/cu)f Multi-foil Filler

Vacuum Brazing of C/C Composite and TiAl Intermetallic Alloy Using BNi-2 Brazing Filler Metal

Interfacial microstructure and mechanical properties of TiAl and C/SiC joint brazed with TiH2-Ni-B brazing powder

Effect of C/C Composite Surface Pretreatment on Properties of Brazed Joint

Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

Microstructure and Mechanical Properties of C/C Composite/ti6al4v Joints with a Cu/TiCuZrNi Composite Brazing Alloy

Microstructure Evolution and Brazing Mechanism of Ti5Si3/Ti3Al Composite and Ni-based Superalloy Joints Using Ti-Zr-Cu-Ni Filler Alloy

Interfacial microstructure and properties of TiAl joints brazed with composite filler reinforced by particles

Active Brazing of C/C Composites and Single Crystal Ni-based Superalloy: Interfacial Microstructure and Formation Mechanism

Research on the Interfacial Structure and Properties of TiAl - Si3N4f/Si3N4 Brazed Joints

Brazing C/SiC Composites and Nb with TiNiNb Active Filler Metal

Microstructure and properties of the C/C-superalloy brazed joint by Ni-based filler

Brazing of C/C composites and 304 stainless steels via Ni/Mo composite interlayer

Brazing of C/C Composites and GH3044 Ni-Based Superalloy Using Ni71 CrSi as the Interlayer

Effect of Ti content on microstructure and mechanical properties of SiCf/SiC composites/GH536 superalloy joints brazed with CoFeCrNiCuTi high entropy filler

Brazing Mechanisms of the Ti2AlC Joints Using a Pure Al Filler Metal

Active Brazing Carbon/carbon Composite to TC4 with Cu and Mo Composite Interlayers

Effect of Brazing Parameters on Microstructure and Mechanical Properties of Ti5Si3/Ti3Al Composite Joints Brazed with Ti–Zr–Cu–Ni Filler Alloy

A Novel Method for Reducing the Brazing Temperature of C/C Composite with TiZrHfTa/Ni Composite Interlayers

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler