Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler
Jia Yang,Xunye Zhang,Guanglu Ma,Panpan Lin,Yanqiang Xu,Tiesong Lin,Peng He,Weimin Long,Jian Li
DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.08.065
IF: 5.7
2021-04-01
Journal of the European Ceramic Society
Abstract:<p>A new Au-Cu-Ti filler featuring superior mechanical properties was developed to enable the brazing of a SiC<sub>f</sub>/SiC composite (CMCs) to itself and a Ni-based superalloy (GH536). The progression of the interfacial reactions was studied using a combination of thermodynamic calculations and experimental observations. It was found that the interfacial reaction was Ti-dominant at the early brazing stage and then gradually transformed to Ni-dominant with the continuous dissolution of the GH536 substrate. Thus, the typical microstructure of GH536/Ti-Ni-Cr-Fe+(Au, Cu)ss + MoNiSi/Ni-Cr-Fe-Si-C (Ni<sub>2</sub>Si + Fe<sub>2</sub>Si + Cr<sub>3</sub>C<sub>2</sub>)+(Au, Cu)ss/Ni<sub>2</sub>Si + TiC+(Au, Cu)ss/ Cr<sub>3</sub>C<sub>2</sub>+Ni<sub>2</sub>Si + TiC + Fe<sub>2</sub>Si/CMCs could be described by the following three stages: a Ti-dominated stage, full interdiffusion stage, and Ni-dominated stage. A maximum shear strength of 36 MPa was obtained for joints brazed at 1050℃ for 10 min, at which a failure occurred at the CMCs/brazing seam interface. The control of the interfacial reactions and the stress relaxation of (Au, Cu)ss contributed to the superior mechanical performance of the composite.</p>
materials science, ceramics