Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates
Haiyan Chen,Xin Nai,Shuai Zhao,Decai Lu,Zhikang Shen,Wenya Li,Chenyang Lu,Jian Cao
DOI: https://doi.org/10.1111/jace.18347
IF: 4.186
2022-02-04
Journal of the American Ceramic Society
Abstract:Reducing the residual stresses and improving the mechanical strength of large-scale ceramic/metal brazing joints is an important problem that must be solved for its practical engineering application. Using composite filler with solid-state phase transformation ceramic particulates, it is theoretically feasible to relieve the residual stress and improve the mechanical properties of ceramic/metal brazed joints. In this study, Cu mesh, Ag-28Cu-2Ti (wt.%), and YSZ (0.6 mol.% Yttria-stabilized Zirconia solid-state phase transformation ceramic particulates) composite power fillers were used in the brazing of Ti3SiC2 ceramic and pure copper. The microstructure of joints and YSZ particulates in the interface was investigated and confirmed by SEM, EDS, STEM and TEM. In addition, the effect of YSZ particulates content on the mechanical properties of joints was investigated and evaluated by the shear strength. The results show that the interfacial phases were mainly Ti5Si3, TiC, TixCu, Ag (s, s), Cu (s, s) and YSZ particulates. Moreover, most of YSZ particulates undergo the solid-state phase transformation from t-ZrO2 to m-ZrO2 during the cooling process of brazing. The abnormal volume expansion of the solid-state phase transformation reduced the thermal mismatch between Ti3SiC2 ceramic and filler, thereby reducing the residual stress in the interface of joint. When using composite filler with 6wt.% YSZ particulates, the shear strength of Ti3SiC2/Cu joint reached the maximum. The maximum average shear strength of the joints was 80.2 MPa, which was about 103.6% more than the joint without YSZ particulates.This article is protected by copyright. All rights reserved
materials science, ceramics