Abstract:Although inorganic all-solid-state Li-ion batteries (ASSLiBs) using stable oxide solid electrolytes are considered to be promising candidates for future energy storage devices, their relatively high cell impedance due to the restricted contact area and interfacial stability results in unsatisfactory electrochemical performance and fast capacity fading. The mechanism limiting performance and cycle life in such ASSLiBs still lack study and hence understanding. To overcome this bottleneck, we prepared a bulk ASSLiB, where a MnO2–CNT nanocomposite is used as a high-voltage anode to prevent reduction of the electrolyte by a lithium anode, high-voltage LiNi0.5Mn1.5O4 is used as a cathode, and ambient-air stable Li1.5Al0.5Ge1.5(PO4)3 (LAGP) is chosen as a solid-state electrolyte (SSE). This ASSLiB shows a maximum discharge capacity of 82 mAh g–1 at 0.15C and 23.8 °C. The electrochemical impedance study of the cell reveals a decrease in impedance after solid interface layer formation in cycle 1 followed by an increase after electrode lithiation/delithiation. Electrochemical evaluation and first-principles calculations were used to explore the decomposition of the LAGP after charge/discharge cycles. Decomposition of LAGP with the assistance of Li ions and free electrons from voids and grain boundaries leads mainly to the formation of Li4P2O7, Li3PO4, Ge5P6O25, AlPO4, and GeO. Finite element method simulations reveal that the volume expansion due to the formation of the decomposition products Li4P2O7, Li3PO4, and AlPO4 results in a maximum internal stress of 2.5–125 GPa for various Li excess ratios ranging from 0 to 6. This by far exceeds the failure stress of LAGP and results in crack formation and growth in the SSE on multiple cycling.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.1c01564.Characteristics of the MnO2–CNT nanocomposite; Nyquist plots; CV curve; TOF-SIMS preparation and characterization; SEM images; formation energy analysis of the LAGP decomposition products; FEM model and parameters; and cycle performance comparison (PDF)This article has not yet been cited by other publications.

Interfacial Stability of Phosphate-NASICON Solid Electrolytes in Ni-Rich NCM Cathode-Based Solid-State Batteries

Stabilized Cathode/Sulfide Electrolyte Interface through Conformally Interfacial Nanocoating for All-Solid-State Batteries

Recent Advances in Li1+xAlxTi2−x(PO4)3 Solid-State Electrolyte for Safe Lithium Batteries

Origin and regulation of interfacial instability for nickel-rich cathodes and NASICON-type Li1+xAlxTi2−x(PO4)3 solid electrolytes in solid-state lithium batteries

Stabilization the Interface of NASICON-type Solid Electrolyte and Li metal by Al Interlayer

Chemomechanical Failure Mechanism Study in NASICON-Type Li1.3Al0.3Ti1.7(PO4)3 Solid-State Lithium Batteries

Single-Crystal-Layered Ni-Rich Oxide Modified by Phosphate Coating Boosting Interfacial Stability of Li10 SnP2 S12 -Based All-Solid-State Li Batteries.

Quasi-Solid-State Lithium Metal Batteries Using the LiNi0.8Co0.1Mn0.1O2-Li1+ xAlxTi2- x(PO4)3 Composite Positive Electrode

Insight into the Extreme Side Reaction between LiNi<sub>0.5</sub>Co<sub>0.2</sub>Mn<sub>0.3</sub>O<sub>2</sub> and Li<sub>1.3</sub>Al<sub>0.3</sub>Ti<sub>1.7</sub>(PO<sub>4</sub>)<sub>3</ sub> during Cosintering for All-Solid-State Batteries

Stabilizing LATP Electrolyte Interface of All-Solid-State Lithium Ion Batteries Consisting of High-Voltage Cathode

Stabilizing the Interface of NASICON Solid Electrolyte Against Li Metal with Atomic Layer Deposition.

Localization of electrons within interlayer stabilizes NASICON-type solid-state electrolyte

Improving the stability of NASICON-type electrolyte with Li metal anode by interfacial modification

Stabilizing the NASICON Solid Electrolyte in an Inert Atmosphere as a Function of Physical Properties and Sintering Conditions for Solid-State Battery Fabrication

Electromechanical Failure of NASICON-Type Solid-State Electrolyte-Based All-Solid-State Li-Ion Batteries

Slurry-Coated LiNi0.8Co0.1Mn0.1O2-Li3InCl6 Composite Cathode with Enhanced Interfacial Stability for Sulfide-Based All-Solid-State Batteries.

Progress and Perspective of Li 1 + X Al X Ti 2 ‐x ( PO 4 ) 3 Ceramic Electrolyte in Lithium Batteries

Manipulating interfacial stability of LiNi0.5Co0.3Mn0.2O2 cathode with sulfide electrolyte by nanosized LLTO coating to achieve high-performance all-solid-state lithium batterie

Stabilization of NASICON-Type Electrolyte against Li Anode via an Ionic Conductive MOF-Incorporated Adhesive Interlayer

Unraveling Interfacial Compatibility of Ultrahigh Nickel Cathode and Chloride Solid Electrolyte for Stable All-Solid-state Lithium Battery

In situ generated polymer electrolyte coating-based Janus interfaces for long-life LAGP-based NMC811/Li metal batteries