Effect of c-BN on the microstructure and high temperature wear resistance of laser cladded Ni-based composite coating
Yue Zhao,Ruifeng Li,Mingfang Wu,Hangyu Yue,Taotao Li,Yuan Chen
DOI: https://doi.org/10.1016/j.surfcoat.2021.127466
IF: 4.865
2021-09-01
Surface and Coatings Technology
Abstract:<p>In this study, Ni-based Ni60+Cu/h-BN+MoO<sub>3</sub> and Ni60+Cu/c-BN+MoO<sub>3</sub> composite coatings were fabricated by laser cladding on a Q235 substrate. Compare with the addition of h-BN, the effect of c-BN on the microstructure, high temperature hardness and wear resistance properties of the coating from 25 °C to 800 °C were analyzed. The results show that part of c-BN is decomposed during laser cladding process, resulting in the formation of Cr(Mo)B, Cr<sub>5</sub>B<sub>3</sub>, CrN and MoN reinforcements. The periphery of the remaining c-BN particle is allotropic transformed to h-BN under laser irradiation. The content of the reinforcement in the coating is increased and the distribution is more uniform, therefore, the hardness of the coating is increased. This resulted in a reduction of the wear rate from 25 °C, 200 °C, 400 °C, 600 °C to 800 °C by 77%, 61%, 29%, 46% and 39%, respectively. The abrasive and adhesive wear are released because of the increasing of deformation resistance and interface strength of γ-(Ni, M) matrix and Cr(Mo)B. In the meantime, the formation of h-BN provides lubricating property over the wide temperature range.</p>
physics, applied,materials science, coatings & films