Abstract:To improve the applicability of a-C coatings in a wide temperature range, a novel Si- and WC- co-reinforced amorphous carbon coating (SiC-nWCC), consisting of Si-doped a-C nanolayers and WC/a-C nano-multilayers, is proposed in this paper. A series of SiC-nWCC coatings with different modulation ratios (0.49–1.98) were fabricated by a closed field unbalanced magnetron sputtering system. The influences of modulation ratio on the microstructure, mechanical properties together with thermal stability of SiC-nWCC coatings were explored. The tribological behaviors of SiC-nWCC coatings against M50 steel balls were investigated at room temperature to 500 °C in ambient air. The results show that the SiC-nWCC coating with the modulation ratio of 1.98 achieved superior wide-temperature applicability, featuring the average friction coefficient lower than 0.17 and the wear rate less than 9.84 × 10 −6 mm 3 /N·m in the whole temperature range of 25–500 °C. The excellent wide-temperature tribological performance of the SiC-nWCC coating are mainly attributed to the good thermal stability and the formation of temperature adaptive tribological layers. At 25 °C, sp 2 -rich carbon is the main lubrication phase of tribological layers, and at 200– 400 °C, the lubrication performance of coating relies on both sp 2 -rich carbon and Si-rich oxides, and at 500 °C, the self-lubrication phases of Si-rich oxides and WO 3 are account for the outstanding lubricating performance of coating. This work provides a profound insight for developing the wide-temperature applicable a-C based coatings.

Microstructure, mechanical and high-temperature tribological properties of amorphous SiC films by pulsed magnetron sputtering

Growth and Mechanical Properties of Amorphous and Nanostructured SiC films

Elevated temperature tribological properties of a-C:Si films sputtered from SiC target in the presence of C2H2 gas

Structural and mechanical properties of amorphous Si–C-based thin films deposited by pulsed magnetron sputtering under different sputtering powers

Crystallization of Amorphous SiC and Superhardness Effect in CrAlN/SiC Nanomultilayered Films

Comparative Study of High Temperature Anti-Oxidation Property of Sputtering Deposited Stoichiometric and Si-rich SiC Films

Microstructure and mechanical property of high growth rate SiC via continuous hot‐wire CVD

Tribological Behavior of MoS2/a-C:Si Composite Films in High-Temperature Air and Vacuum Environments

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water

Influence of Si on the Microstructure and Mechanical and Tribological Properties of Ag/a-C:H Films

Structural and tribological behaviours of silicon doped amorphous carbon films

Tribological behavior of MoS 2 /a-C:Si composite films in high-temperature air and vacuum environments

The role of Si on the structure and tribological properties of a-C:H:Ni soft films at elevated temperatures

Effect of Si Content on the Tribological Properties of Crsin Films in Air and Water Environments

Influence of radio frequency magnetron sputtering parameters on the structure and performance of SiC films

Tribological behavior of a novel Si- and WC- co-reinforced a-C multilayer coating at 25– 500 °C

Microstructure and Tribological Properties of Ti-contained Amorphous Carbon Film Deposited by DC Magnetron Sputtering

Tribology dependence on both structures of bulk a-C:H:Si films and transfer layer via adjustable Si content

Microstructure, Mechanical and Tribological Properties of Si and Al Co-Doped Hydrogenated Amorphous Carbon Films Deposited at Various Bias Voltages

SiC film deposition by DC magnetron sputtering

Effect of silicon-doping on the wide-temperature tribological behavior and lubrication mechanism of WC/a-C film