Microstructure and mechanical properties of SiC reinforced AlSi10Mg composites fabricated by laser metal deposition

Xin Xi,Bo Chen,Caiwang Tan,Xiaoguo Song,Jicai Feng

DOI: https://doi.org/10.1016/j.jmapro.2020.08.073

IF: 5.684

2020-10-01

Journal of Manufacturing Processes

Abstract:<p>In this study, SiC/AlSi10Mg aluminum matrix composites (AMCs) were fabricated by laser metal deposition (LMD), and the effects of SiC content on microstructure, microhardness, wear performance and tensile properties were investigated. After LMD processing, the diffraction angle of the highest diffraction peak of the α-Al phase changed from 38.470° to 44.833°, demonstrating a clear preferred orientation. Si and Mg elements gathered at the grain boundaries in form of Si and Mg₂Si phases. The presence of SiC promoted the aggregation of Fe elements, forming the needle-like Al-Fe-Si eutectic phase. As the SiC content increased, the grain size of the middle area decreased and the randomness of the texture distribution increased. Furthermore, the AMCs with 2wt.% SiC exhibited impressive comprehensive performances, i.e., microhardness of 117.06 HV, a wear rate of 1.84×10⁻³ mm³N^-1m^-1 and tensile strength of 219.04MPa. The wear resistance was improved and the wear mechanism changed from adhesive wear to abrasive wear with the addition of SiC participles.</p>

engineering, manufacturing

What problem does this paper attempt to address?

The problem this paper attempts to address is the preparation of SiC-reinforced AlSi10Mg aluminum matrix composites (AMCs) using Laser Metal Deposition (LMD) technology, and the study of the effects of SiC content on the microstructure, microhardness, wear resistance, and tensile properties of the composites. Specifically, the paper focuses on the following aspects:

1. **Microstructure Optimization**: Investigating how the addition of SiC particles affects the microstructure of the composites, including changes in grain morphology, grain boundary distribution, and phase composition.
2. **Mechanical Performance Enhancement**: Evaluating the impact of different SiC contents on the microhardness, wear resistance, and tensile strength of the composites to determine the optimal SiC content.
3. **Wear Mechanism Changes**: Analyzing how the addition of SiC particles alters the wear mechanism of the composites, transitioning from adhesive wear to abrasive wear.

Through these studies, the paper aims to reveal the mechanisms of microstructure optimization and performance enhancement of SiC particle-reinforced aluminum matrix composites in the LMD process, laying the foundation for the use of LMD technology to manufacture high-performance aluminum alloy components.