Abstract:Yttria-stabilized zirconia (YSZ)/gadolinia-doped ceria (GDC) dual-layered electrolytes have promising potential in solid oxide fuel cells (SOFCs) to prevent the destroying reaction of the lanthanum-containing cathode with ZrO2 base electrolyte and improve ionic conduction by blocking ceria based electrolyte electronic conduction. Preparation of the YSZ/GDC electrolyte is problematic due to the formation of a high electrical resistance interdiffusion layer at high sintering temperatures. Flash sintering (FS) is a promising method for sintering materials at low temperatures and short times. Herein, FS is used to limit the interdiffusion layer. The green dual-layered electrolytes are prepared by YSZ tape casting and coating the GDC layer on the binder-burnout YSZ layer by wet spraying method. The effect of electric field strength (E) and current density (J) on the interdiffusion layer thickness is investigated by the response surface methodology (RSM). The interdiffusion layer thickness in the electrolytes is determined using elemental distribution curves across the YSZ/GDC interface using a scanning electron microscope (SEM) equipped with an energy-dispersive X-ray spectrometer (EDS). Response surface of interdiffusion layer thickness shows that the electric field strength is more effective in the interdiffusion layer propagation than the current density. By controlling the electric field strength and current density, the interdiffusion layer is limited and descends from 45 µm for E = 300 V/cm and J = 200 mA/mm2 to 1 µm for E = 80 V/cm and J = 200 mA/mm2 as the optimum FS parameters. Electrochemical impedance spectroscopy (EIS) results show improved electrical conduction in optimal flash sintered electrolytes compared with conventionally sintered ones due to the thinner interdiffusion layer. The SOFC single cell is made using the optimal flash sintered YSZ/GDC electrolyte, which shows a performance of 0.3 W/cm2 at 800 °C, about 15% higher than the SOFC single cell made by conventionally sintered YSZ/GDC electrolyte.

Performance of a double-layer CGO/YSZ electrolyte for solid oxide fuel cells

A simple and easy one-step fabrication of thin BaZr0.1Ce0.7Y0.2O3−δ electrolyte membrane for solid oxide fuel cells

Solid oxide fuel cell with a spin-coated yttria stabilized zirconia/gadolinia doped ceria bi-layer electrolyte

Interdiffusion between gadolinia doped ceria and yttria stabilized zirconia in solid oxide fuel cells: Experimental investigation and kinetic modeling

Boosting intermediate temperature performance of solid oxide fuel cells via a tri‐layer ceria–zirconia–ceria electrolyte

High Performance Gd3+ and Y3+ Co-Doped Ceria-Based Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

Synthesis and Characterization of Gadolinium-Doped Zirconia as a Potential Electrolyte for Solid Oxide Fuel Cells

Application of a Triple-Conducting Heterostructure Electrolyte of Ba0.5Sr0.5Co0.1Fe0.7Zr0.1Y0.1O3−δ and Ca0.04Ce0.80Sm0.16O2−δ in a High-Performance Low-Temperature Solid Oxide Fuel Cell

Preparation, Evaluation, and Application of SUS430/441 Interconnect with Mn-Co Coating in Solid Oxide Fuel Cells

Optimization of ScSZ/GDC bilayer thin film electrolyte for anodic aluminum oxide supported low temperature solid oxide fuel cells

Synthesis and Characterization of (gd, Y)-Doped Ceria Electrolytes for Solid Oxide Fuel Cell

Electrical properties of CeO2-Y2O3 electrolyte SOFCs

High-performing and stable semiconductor yttrium-doped gadolinium electrolyte for low-temperature solid oxide fuel cells

Low Temperature Deposited (ce,gd)o2−x Interlayer for La0.6Sr0.4Co0.2Fe0.8O3 Cathode Based Solid Oxide Fuel Cell

High-performing and stable non-doped ceria electrolyte with amorphous carbonate coating layer for low-temperature solid oxide fuel cells

Controlling Yttria-stabilized zirconia/gadolinia-doped ceria interdiffusion layer in the solid oxide fuel cell electrolyte via flash sintering method

High performance and stability of nanocomposite oxygen electrode for solid oxide cells

Sputter-deposited medium-temperature solid oxide fuel cells with multi-layer electrolytes

Bilayered BaZr 0.1 Ce 0.7 Y 0.2 O 3-δ /Ce 0.8 Sm 0.2 O 2-δ electrolyte membranes for solid oxide fuel cells with high open circuit voltages

Two-Layer Fuel Cell Electrolyte Structure by Sol-Gel Processing

Fabrication of YSZ/SNDC Bilayer Electrolytes by Spark Plasma Sintering